Poly-ε-Caprolactone-Hydroxyapatite-Alumina (PCL-HA-α-Al2O3) Electrospun Nanofibers in Wistar Rats.

Biodegradable polymers of natural origin are ideal for the development of processes in tissue engineering due to their immunogenic potential and ability to interact with living tissues. However, some synthetic polymers have been developed in recent years for use in tissue engineering, such as Poly-ε-caprolactone. The nanotechnology and the electrospinning process are perceived to produce biomaterials in the form of nanofibers with diverse unique properties. Biocompatibility tests of poly-ε-caprolactone nanofibers embedded with hydroxyapatite and alumina nanoparticles manufactured by means of the electrospinning technique were carried out in Wistar rats to be used as oral dressings. Hydroxyapatite as a material is used because of its great compatibility, bioactivity, and osteoconductive properties. The PCL, PCL-HA, PCL-α-Al2O3, and PCL-HA-α-Al2O3 nanofibers obtained in the process were characterized by infrared spectroscopy and scanning electron microscopy. The nanofibers had an average diameter of (840 ± 230) nm. The nanofiber implants were placed and tested at 2, 4, and 6 weeks in the subcutaneous tissue of the rats to give a chronic inflammatory infiltrate, characteristic foreign body reaction, which decreased slightly at 6 weeks with the addition of hydroxyapatite and alumina ceramic particles. The biocompatibility test showed a foreign body reaction that produces a layer of collagen and fibroblasts. Tissue loss and necrosis were not observed due to the coating of the material, but a slight decrease in the inflammatory infiltrate occurred in the last evaluation period, which is indicative of the beginning of the acceptance of the tested materials by the organism.

Epithelial Growth Factor-Anchored on Polycaprolactone/6-deoxy-6-amino-ß-cyclodextrin Nanofibers: In Vitro and In Vivo Evaluation.

Polycaprolactone (PCL) is a well-known FDA approved biomaterial for tissue engineering. However, its hydrophobic properties limit its use for skin wound healing which makes its functionalization necessary. In this work, we present the fabrication and evaluation of PCL nanofibers by the electrospinning technique, as well as PCL functionalized with 6-deoxy-6-amino-ß-cyclodextrin (aminated nanofibers). Afterwards, epithelial growth factor (EGF) was anchored onto hydrophilic PCL/deoxy-6-amino-ß-cyclodextrin. The characterization of the three electrospun fibers was made by means of field emission scanning electron microscopy (FESEM), Fourier transform infrared spectroscopy-attenuated total reflectance (FTIR-ATR); Confocal-Raman Spectroscopy were used for elucidated the chemical structure, the hydrophilicity was determined by Contact Angle (CA). In vitro cell proliferation test was made by seeding embryonic fibroblast cell line (3T3) onto the electrospun mats and in vivo studies in a murine model were conducted to prove its effectivity as skin wound healing material. The in vitro studies showed that aminated nanofibers without and with EGF had 100 and 150% more cell proliferation of 3T3 cells against the PCL alone, respectively. In vivo results showed that skin wound healing in a murine model was accelerated by the incorporation of the EGF. In addition, the EGF had favorable effects in epidermal cell proliferation. The study demonstrates that a protein of high biological interest like EGF can be attached covalently to the surface of a synthetic material enriched with amino groups. This kind of biomaterial has a great potential for applications in skin regeneration and wound healing.

Polycaprolactone/Amino-ß-Cyclodextrin Inclusion Complex Prepared by an Electrospinning Technique.

Electrospun scaffolds of neat poly-ε-caprolactone (PCL), poly-ε-caprolactone/ß-cyclodextrin inclusion complex (PCL/ß-CD) and poly-ε-caprolactone amino derivative inclusion complex (PCL/ß-CD-NH2) were prepared by the electrospinning technique. The obtained mats were analyzed by a theoretical model using the Hartree⁻Fock method with an STO-3G basis set, and characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), Fourier transform infrared spectroscopy-attenuated total reflectance (FTIR-ATR), differential scanning calorimetry (DSC), confocal-Raman spectroscopy, proton nuclear magnetic resonance (¹HNMR) and contact angle measure (CA). Different mixtures of solvents, such as dimethylformamide (DMF)-tetrahydrofuran (THF), dichlormethane (DCM)-dimethyl sulfoxide (DMSO) and 2,2,2-Trifluoroethanol (TFE), were tested in the fiber preparation. The results indicate that electrospun nanofibers have a pseudorotaxane structure and when it was prepared using a 2,2,2-Trifluoroethanol (TFE) as solvent, the nanofibers were electrospun well and, with the other solvents, fibers present defects such as molten fibers and bead-like defects into the fiber structure. This work provides insights into the design of PCL/ß-CD-NH2 based scaffolds that could have applications in the biomedical field.