DLC coatings: effects of physical and chemical properties on biological response.

Recent trials on diamond-like carbon (DLC) coated medical devices have indicated promise for blood interfacing applications. The literature is sparse regarding structural and compositional effects of DLC on cellular response. An important goal in optimizing blood-interfacing implants is minimal macrophage attachment, and maximal albumin:fibrinogen adsorption ratio. DLC coatings deposited by PACVD and FAD, were analysed with respect to sp3 content (EELS), hydrogen content (ERDA), surface composition (XPS), surface roughness (AFM), surface energy, albumin:fibrinogen adsorption ratio, and macrophage viability and attachment. We found that increasing surface roughness and surface energy enhanced the macrophage viability and the albumin:fibrinogen adsorption ratio. We also found that the higher the hydrogen content for a-C:Hs deposited by PACVD, the lower the albumin:fibrinogen adsorption ratio, and macrophage attachment. This suggests that hydrogen content may be an important factor for influencing the biological response of DLC surfaces. Macrophage cells spread well on all DLC surfaces, and the surface results indicated the non-toxic nature of the surfaces on the cells at the time points tested.

Mechanical characteristics of optical coatings prepared by various techniques: a comparative study.

Good performance of optical coatings depends on the appropriate combination of optical and mechanical properties. Therefore, successful applications require good understanding of the relationship between optical microstructural and mechanical characteristics and film stability. In addition, there is a lack of standard mechanical tests that allow one to compare film properties measured in different laboratories. We give an overview of the methodology of mechanical measurements suitable for optical coatings; this includes depth-sensing indentation, scratch resistance, friction, abrasion and wear testing, and stress and adhesion evaluation. We used the techniques mentioned above in the same laboratory to systematically compare the mechanical behavior of frequently used high- and low-index materials, namely, TiO2, Ta2O5, and SiO2, prepared by different complementary techniques. They include ion-beam-assisted deposition by electron-beam evaporation, magnetron sputtering, dual-ion-beam sputtering, plasma-enhanced chemical-vapor deposition, and filtered cathodic arc deposition. The mechanical properties are correlated with the film microstructure that is inherently related to energetic conditions during film growth.