Influence of Restorative Material on the Distribution of Loads to the Bone in Hybrid Abutment Crowns-In Vitro Study.

Background: The objective of this study was to evaluate the load transmitted to the peri-implant bone by seven different restorative materials in single-unit rehabilitations with morse taper implants using a strain gauge. Materials: In a polyurethane block that simulated type III bone, a morse taper platform implant was installed (3.5 × 11 mm) in the center and 1 mm below the test base surface, and four strain gauges were installed around the implant, simulating the mesial, distal, buccal and lingual positions. Seven similar hybrid abutment crowns were crafted to simulate a lower premolar using different materials: 1-PMMA; 2-glass ceramic over resin matrix; 3-PEEK + lithium disilicate; 4-metal-ceramic; 5-lithium disilicate; 6-zirconia + feldspathic; 7-monolithic zirconia. All groups underwent axial and oblique loads (45 degrees) of 150 N from a universal testing machine. Five measurements (n = 5) were performed with each material and for each load type; the microdeformation data underwent statistical analysis. The data were obtained in microdeformation (µÎµ), and the significance level was set at p ≤ 0.05. Results: There was no statistically significant difference in the evaluation among the materials under either the axial load or the oblique load at 45 degrees. In turn, in the comparison between axial load and oblique load, there was a difference in load for all materials. Conclusion: The restorative material did not influence the load transmitted to the bone. Furthermore, the load transmitted to the bone was greater when it occurred obliquely at 45° regardless of the material used. In conclusion, it appeared that the different elastic modulus of each material did not influence the load transmission to the peri-implant bone.

Randomized Clinical Trial Comparing Insertion Torque and Implant Stability of Two Different Implant Macrogeometries in the Initial Periods of Osseointegration.

Objectives: The present study compared two implants with different macrogeometries placed in healed alveolar sites, evaluating the insertion torque (ITV) and implant stability quotient (ISQ) values at three different periods. Methods: Seventy patients with a total of 100 dental implants were allocated into two groups (n = 50 per group): DuoCone implants (DC group) that included 28 implants in the maxilla and 22 in the mandible, and Maestro implants (MAE group) that included 26 in the maxilla and 24 in the mandible. The ITV was measured during the implant placement, and the ISQ values were measured immediately at implant placement (baseline) and after 30 and 45 days. Results: The mean and standard deviations of the ITV were statistically significant (p < 0.0001), 56.4 ± 6.41 Ncm for the DC group and 29.3 ± 9.65 Ncm for the MAE group. In the DC group, the ISQs ranged between 61.1 ± 3.78 and 69.8 ± 3.86, while the MAE group presented similar values compared with the other group, ranging between 61.9 ± 3.92 and 72.1 ± 2.37. Conclusions: The value of implant insertion torque did not influence the ISQ values measured immediately after implant placement. However, the ITV influenced the ISQ values measured in the two initial periods of osseointegration, with implants installed with lower torques presenting higher ISQ values.