Development of Test Methods to Evaluate the Printability of Concrete Materials for Additive Manufacturing.

This study proposes test methods for assessing the printability of concrete materials for Additive Manufacturing. The printability of concrete is divided into three main aspects: flowability, setting time, and buildability. These properties are considered to monitor the critical quality of 3DCP and to ensure a successful print. Flowability is evaluated through a rheometer test, where the evolution of shear yield strength is monitored at a constant rate (rpm), similar to the printer setup. Flowability limits were set based on the user-defined maximum thickness of a printed layer and the onset of gaps/cracks during printing. Setting time is evaluated through an ultrasonic wave pulse velocity test (UPV), where the first inflection point of the evolution of the UPV graph corresponds to the setting time of the concrete specimen. The results from this continuous non-destructive test were found to correlate with the results from the discrete destructive ASTM C-191 test for measuring setting time with a maximum difference of 5% between both sets of values. Lastly, buildability was evaluated through the measurement of the early-age compressive strength of concrete, and a correlation with the UPV results obtained a predictive model that can be used in real-time to non-destructively assess the material buildability. This predictive model had a maximum percentage difference of 13% with the measured values. The outcome of this study is a set of tests to evaluate the properties of 3D printable concrete (3DP) material and provide a basis for a framework to benchmark and design materials for additive manufacturing.

Properties and Microstructure Distribution of High-Performance Thermal Insulation Concrete.

The aim of this experimental study is to develop high strength and lightweight concrete mixture suitable for structural applications. This work investigates the effect of replacing normal aggregate either partially or totally with expanded perlite aggregate. This material allows for better thermal insulation properties, thus decreasing the energy usage within the life cycle of the concrete structure. Expanded perlite aggregate was used in concrete by 20%, 40%, 60%, 80%, and 100% in replacement of the natural aggregate. Material characterization tests of compressive strength, flexural strength, and thermal conductivity were carried out for six concrete mixtures. In addition, microstructure analysis was performed with the aid of a micro-computed tomography system to investigate the effects and relation of microstructure quantities on material properties. The proposed concrete mixture, which has 100% of expanded perlite aggregate, has a unit weight of 1703 kg/m3 and achieved reduction percentage of thermal conductivity around 62% (1.81 to 0.69 W·m-1·K-1) and a compressive strength of 42 MPa at 28 days; and thus is ideal for structural applications with enhanced properties.

Evolution of the microstructure of unmodified and polymer modified asphalt binders with aging in an accelerated weathering tester.

This paper presents findings on the evolution of the surface microstructure of two asphalt binders, one unmodified and one polymer modified, directly exposed to aging agents with increasing durations. The aging is performed using an accelerated weathering tester, where ultraviolet radiation, oxygen and an increased temperature are applied to the asphalt binder surface. Ultraviolet and dark cycles, which simulated the succession of day and night, alternated during the aging process, and also the temperature varied, which corresponded to typical summer day and night temperatures registered in the state of Qatar. Direct aging of an exposed binder surface is more effective in showing microstructural modifications than previously applied protocols, which involved the heat treatment of binders previously aged with standardized methods. With the new protocol, any molecular rearrangements in the binder surface after aging induced by the heat treatment is prevented. Optical photos show the rippling and degradation of the binder surface due to aging. Microstructure images obtained by means of atomic force microscopy show gradual alteration of the surface due to aging. The original relatively flat microstructure was substituted with a profoundly different microstructure, which significantly protrudes from the surface, and is characterized by various shapes, such as rods, round structures and finally 'flower' or 'leaf' structures.