RESUMO
In this work, an efficient 3-step process targeting the chemical modification and purification of lignin oligomers from industrial alkaline lignin is described. The oxidative depolymerization process of alkaline lignin with O2 or Air pressure, without use of metal catalyst, led to the production of two fractions of lignin oligomers named 'precipitated lignin' and 'hydrosoluble lignin' with 40% and 60% yield, respectively. These fractions were characterized with a wide range of methods including NMR spectroscopy (31P, 2D-HSQC), SEC (in basic media), FTIR. NMR analyses revealed the presence of carboxylic acid functions at a ratio of 1.80 mmol/g and 2.80 mmol/g for the precipitated and hydrosoluble lignin, respectively, values much higher than what is generally found in native lignin (between 0.2 and 0.5 mmol/g). SEC analyses revealed the formation of low molar masses for the precipitated (2200 g/mol) and hydrosoluble fractions (1500 g/mol) in contrast to the alkaline lignin (3900 g/mol). It is worth noting that the hydrosoluble fraction of lignin is soluble in water at any pH. Both processes (oxygen and air) were successfully scaled up and showed similar results in terms of yield and functionalization.
RESUMO
Hemicelluloses were extracted from a softwood acid sulfite pulp in a three-step procedure. Further delignification step resulted in a holocellulose pulp containing only 1.7 wt.% of the lignin left. Cold caustic extraction (CCE) with 18 wt.% NaOH at 60 °C for 1 h was performed to solubilize hemicelluloses of the holocellulose. An unbleached cellulose pulp was then obtained 97% pure, which indicates that 89% of the hemicelluloses were removed. After purification, extraction yields between 1.1 wt.% and 9.5 wt.% were obtained from the delignified pulp and the hemicelluloses' chemical compositions and structures were investigated by 1H, 13C nuclear magnetic resonance spectroscopy (NMR) and two-dimensional NMR by correlation spectroscopy (2D-COSY) and proton-detected heteronuclear single-quantum correlation (2D-HSQC), high-performance anion-exchange chromatography coupled with a pulsed amperometry detector (HPAEC-PAD), size-exclusion chromatography coupled with a refractive index detector (SEC-RI) and thermogravimetric analyses (TGA). Hemicelluloses were obtained with a purity of 96%, with short cellulosic chains as the only residue. Sulfite pulping modified the hemicelluloses' structure, and it was found that two types of hemicelluloses were isolated, glucomannans, predominant at 67%, and methylglucuronoxylans. Finally, alkali-soluble hemicelluloses displayed relatively narrow size distributions and low molar masses, Mw varying between 18,900 and 30,000 g/mol after acid sulfite pulping.