RESUMO
The three intermetallic compounds SrAuGa, BaAuAl and BaAuGa were synthesised from the elements in niobium ampoules. The Sr compound crystallises in the orthorhombic KHg2 -type structure (Imma, a=465.6(1), b=771.8(2), c=792.6(2)â pm, wR2 =0.0740, 324 F2 values, 13â variables), whereas the Ba compounds were both found to crystallise in the cubic non-centrosymmetric LaIrSi-type structure (P21 3, BaAuAl: a=696.5(1)â pm; wR2 =0.0427, 446 F2 values, 12â variables; BaAuGa: a=693.49(4)â pm, wR2 =0.0717, 447 F2 values, 12â variables). The samples were investigated by powder X-ray diffraction and their structures refined on the basis of single-crystal X-ray diffraction data. The title compounds, along with references from the literature (CaAuAl, CaAuGa, CaAuIn, and SrAuIn), were characterised further by susceptibility measurements and 27 Al and 71 Ga solid-state NMR spectroscopy. Theoretical calculations of the density of states (DOS) and the NMR parameters were used for the interpretation of the spectroscopic data. The electron transfer from the alkaline-earth metals and the groupâ 13 elements onto the gold atoms was investigated through X-ray photoelectron spectroscopy (XPS), classifying these intermetallics as aurides.
RESUMO
The quasibinary section of the intermetallic phases MAl4 and MGa4 with M=Sr and Ba have been characterised by means of X-ray diffraction (XRD) studies and differential thermal analysis. The binary phases show complete miscibility and form solid solutions M(Al1-x Gax )4 with M=Sr and Ba. These structures crystallise in the BaAl4 structure type with four- and five-bonded Al and/or Ga atoms (denoted as Al(4b), Al(5b), Ga(4b), and Ga(5b), respectively) that form a polyanionic Al/Ga sublattice. Solid state 27 Alâ NMR spectroscopic analysis and quantum mechanical (QM) calculations were applied to study the bonding of the Al centres and the influence of Al/Ga substitution, especially in the regimes with low degrees of substitution. M(Al1-x Gax )4 with M=Sr and Ba and 0.925≤x≤0.975 can be described as a matrix of the binary majority compound in which a low amount of the Ga atoms has been substituted by Al atoms. In good agreement with the QM calculations, 27 Alâ NMR investigations and single crystal XRD studies prove a preferred occupancy of Al(4b) for these substitution regimes. Furthermore, two different local Al environments were found, namely isolated Al(4b1) atoms and Al(4b2), due to the formation of Al(4b)-Al(4b) pairs besides isolated Al(4b) atoms within the polyanionic sublattice. QM calculations of the electric field gradient (EFG) using superlattice structures under periodic boundary conditions are in good agreement with the NMR spectroscopic results.
RESUMO
Complete miscibility of the intermetallic phases (IPs) SrGa2 and BaGa2 forming the solid solution Sr(1-x)Ba(x)Ga2 is shown by means of X-ray diffraction, thermoanalytical and metallographic studies. Regarding the distances of Sr/Ba sites versus substitution degree, a model of isolated substitution centres (ISC) for up to 10% cation substitution is explored to study the influence on the Ga bonding situation. A combined application of NMR spectroscopy and quantum mechanical (QM) calculations proves the electric field gradient (EFG) to be a sensitive measure of different bonding situations. The experimental resolution is boosted by orientation-dependent NMR on magnetically aligned powder samples, revealing in first approximation two different Ga species in the ISC regimes. EFG calculations using superlattice structures within periodic boundary conditions are in fair agreement with the NMR spectroscopy data and are discussed in detail regarding their application on disordered IPs.