RESUMO
A new method for pulsed laser deposition of plasmonic silver nanoparticle (NP) films in flowing gas at atmospheric pressure is described. The ablation was done using an excimer laser at 248 nm. Fast optical imaging shows that the ablation plume is captured by the flowing gas, and is expected to form a NP aerosol, which is carried 5-20 mm to the substrate. The dependence of the deposition rate on laser fluence, gas flow velocity, and target-substrate distance was investigated using electron microscopy and absorption spectroscopy of the deposited films. The NP films were annealed in argon and hydrogen at 400 °C, and in air for temperatures in the range 200 °C-900 °C, leading to strong enhancement, and narrowing of the surface plasmon resonance. The films were used for surface enhanced Raman spectroscopy of a 10-5 molar solution of Rhodamine 6G; films annealed in air at 400 °C were five times more sensitive than the as-deposited films.
RESUMO
We describe the soft chemistry synthesis of amine-templated gallium chalcogenide nanotubes through the reaction of gallium(iii) acetylacetonate and the chalcogen (sulfur, selenium) using a mixture of long-chain amines (hexadecylamine and dodecylamine) as a solvent. Beyond their role as solvent, the amines also act as a template, directing the growth of discrete units with a one-dimensional multilayer tubular nanostructure. These new materials, which broaden the family of amine-stabilized gallium chalcogenides, can be tentatively classified as direct large band gap semiconductors. Their preliminary performance as active material for electrodes in lithium ion batteries has also been tested, demonstrating great potential in energy storage field even without optimization.
RESUMO
We report the growth of carbon nanotubes on the size controlled iron catalytic nanoparticles. The nanotubes were grown by thermal chemical vapour deposition (CVD) in the temperature range 600-850 degrees C. The Fe films were deposited on silicon by pulsed laser deposition in vacuum. Atomic force microscopy measurements were performed on the catalytic nanoparticles. The topography of the catalytic nanoparticles shows the homogenous distribution of Fe catalyst. We observe the nanotubes are produced only at temperatures between 650 and 800 degrees C, and within this narrow temperature regime the yield of nanotubes reaches a maximum around 750 degrees C and then declines. Raman measurements illustrate a high G/D peak ratio indicating good nanotube quality. By further defining the size of the catalyst the diameter of these carbon nanotubes can be controlled.