Microstructure, thermooxidation and mechanical behavior of a novel highly linear, vitamin E stabilized, UHMWPE.

A novel, vitamin E-stabilized, medical grade ultra-high molecular polyethylene, MG003 (DSM Biomedical; The Netherlands), has been very recently introduced for use in total joint replacements. This homopolymer resin features average molecular weight similar to that of conventional GUR 1050 resin (5.5-6*10(6)g/mol), but a higher degree of linearity. The aim of this study was to characterize the microstructure, thermal and thermooxidation properties as well as the mechanical behavior of this novel MG003 resin before and after gamma irradiation in air to 90 kGy. For this purpose, a combination of experimental techniques were performed including differential scanning calorimetry (DSC), thermogravimetry (TG), transmission electron microscopy (TEM), X-Ray Diffraction, electron paramagnetic resonance (EPR), and uniaxial tensile tests. As-consolidated MG003 materials exhibited higher crystalline contents (~62%), transition temperatures (~140 °C), crystal thickness (~36 nm), yield stress (~25 MPa) and elastic modulus (~400 MPa) than GUR 1050 controls (55%, 136 °C, 27 nm, 19 MPa, and 353 MPa, respectively). Irradiation produced similar changes in both MG003 and GUR 1050 materials, specifically increased crystallinity (63% and 60%, respectively), crystal thickness (39 nm and 30 nm), yield stress (27 MPa and 21 MPa), but, above of all, loss of elongation to breakage (down to 442 and 469%, respectively). Thermogravimetric and EPR results suggest comparable susceptibilities to oxidation for both MG003 and GUR 1050 polyethylenes. Based on the present findings, MG003 appears as a promising alternative medical grade polyethylene and it may satisfactorily contribute to the performance of total joint replacements.

Influence of gamma irradiation on carbon nanotube-reinforced polypropylene.

Single walled carbon nanotubes (SWNT) have been incorporated into a polypropylene (PP) matrix in different concentrations (range: 0.25-2.5 wt%). The nanotubes were blended with PP particles (approximately 500 microm in size) before mixing in an extruder. Finally, rectangular plates were obtained by compression moulding. PP-SWNT composites were gamma irradiated at different doses, 10 and 20 kGy, to promote crosslinking in the matrix and potentially enhance the interaction between nanotubes and PP. Extensive thermal, structural and mechanical characterization was conducted by means of DSC, X-ray diffraction, Raman spectroscopy, uniaxial tensile tests and dynamic mechanical thermal (DMTA) techniques. DSC thermograms reflected higher crystallinity with increasing nanotube concentration. XRD analysis confirmed the only presence of a monoclinic crystals and proved unambiguously that CNTs generated a preferred orientation. Raman spectroscopy confirmed that the intercalation of the polymer between bundles is favored at low CNTs contents. Elastic modulus results confirmed the reinforcement of the polypropylene matrix with increasing SWNT concentration, although stiffness saturation was observed at the highest concentration. Loss tangent DMTA curves showed three transitions for raw polypropylene. While gamma relaxation remained practically unchanged in all the samples, beta relaxation temperatures showed an increase with increasing CNT content due to the reduced mobility of the system. Gamma-irradiated PP exhibited an increase in the beta relaxation temperature, associated with changes in glass transition due to radiation-induced crosslinking. On the contrary, gamma-irradiated nanocomposites did not show this effect probably due to the reaction of radiative free radicals with CNTs.

Wear resistance of highly cross-linked and remelted polyethylenes after ion implantation and accelerated ageing.

Ion implantation may provide medical polyethylenes with excellent mechanical and tribological properties, helping to lower the risk of long-term osteolysis. Highly crosslinked and remelted polyethylenes, materials currently used as soft components in artificial joints, were implanted with N+ and He+ ions at different ion fluences. The mechanical and tribological properties under distilled water lubrication at body temperature were assessed after ion implantation by means of microhardness and pin-on-disc tests respectively. Thus, the influences of the ionic species and implantation dose on surface hardness, friction coefficient, and wear factor were fully characterized. Furthermore, the tribological behaviour was evaluated after an accelerated ageing protocol (120 degrees C for 36h). Ion implantation increased the surface hardness, as well as friction coefficients, and decreased the wear factors especially at the highest doses. Also, even though all artificially aged materials showed a worse wear behaviour, polyethylenes implanted with either N+ or He+ at the highest doses maintained a relatively good wear factor in comparison with the aged non-implanted material. The origins of these modifications are discussed according to the effects of ion implantation on the microstructure of the polymer.

Influence of the remelting process on the fatigue behavior of electron beam irradiated UHMWPE.

Electron beam irradiation at doses below 150 kGy is a widely used technique to obtain highly crosslinked ultra-high-molecular-weight polyethylene (UHMWPE). Its current use in total joint replacement components may improve wear resistance and decrease UHMWPE particle debris. However, currently used post-irradiation thermal treatments, which aim to decrease the free radicals within the material, introduce microstructural changes that affect UHMWPE mechanical properties, particularly the fatigue strength. This influence may be crucial in total knee replacements, where fatigue-related damage limits the lifespan of the prosthesis. Therefore, more studies are required to understand UHMWPE fatigue after current crosslinking protocols. This study was planned to evaluate the influence of UHMWPE remelting after irradiation on the material fatigue resistance. The remelting was achieved at 150 degrees C for 2 h on UHMWPE previously irradiated at 50, 100, and 150 kGy. Fatigue evaluation included short-term tests under cyclic tensile stress with zero load ratio, R = 0, and 1 Hz. In addition, stress-life testing was performed using 12% yield as the criterion for failure. Near-threshold fatigue crack propagation experiments were also performed at a frequency of 5 Hz, and crack length was measured in nonthermally treated and remelted irradiated UHMWPE. Crystallinity percentage was calculated from DSC measurements. The results pointed out that irradiation positively contributed to total life analysis, but the further remelting process decreased the flaw initiation resistance. On the other hand, both processes negatively affected the fatigue resistance of notched components. From a clinical point of view, the results suggest that the material fatigue behavior should be carefully studied in new UHMWPE to avoid changes related to material processing.

Comparative cyclic stress-strain and fatigue resistance behavior of electron-beam- and gamma-irradiated ultrahigh molecular weight polyethylene.

Fatigue-related damage in UHMWPE is one of the main causes of long-term failure in total joint replacements. Crosslinking ultrahigh molecular weight polyethylene (UHMWPE) by gamma or electron-beam irradiation, in combination with prior or further thermal treatment, enhances its wear resistance against metallic components in total hip replacements, and eventually in knees. However, little information is available on the fatigue response of this modified UHMWPE. The objective of this study was to compare electron-beam-irradiated UHMWPE at 50, 100, and 150 kGy, with the well-known 25 kGy gamma-irradiated UHMWPE. Two different cyclic tests were performed under tensile stress, with a zero load ratio, R = 0. First, specimens were subjected to a sinusoidal load cycle at 1 Hz, which provided stress-life curves with the use of a failure criterion based on 12% yield strain. Second, specimens were tested under 50 load cycles at a displacement rate of 15 mm/min, which provided information about the evolution of secant modulus and plastic strain. The incubation period was also analyzed. DSC measurements were carried out to check the crystallization effect of irradiation. According to the results of fatigue resistance there was a crossover behavior between gamma- and electron-beam-irradiated UHMWPE regarding the applied stress. When the stress was higher than the crossover value, the fatigue resistance of gamma-irradiated samples was higher than electron-beam-irradiated ones. When the stress was lower, the fatigue behavior was the opposite. The crossover stress depended on the electron-beam-irradiation dose. The clinical relevance of this study lies in an improved knowledge of electron-beam-irradiated material under extreme mechanical circumstances, such as fatigue.