A (S)TEM gas cell holder with localized laser heating for in situ experiments.

The advent of aberration correction for transmission electron microscopy has transformed atomic resolution imaging into a nearly routine technique for structural analysis. Now an emerging frontier in electron microscopy is the development of in situ capabilities to observe reactions at atomic resolution in real time and within realistic environments. Here we present a new in situ gas cell holder that is designed for compatibility with a wide variety of sample type (i.e., dimpled 3-mm discs, standard mesh grids, various types of focused ion beam lamellae attached to half grids). Its capabilities include localized heating and precise control of the gas pressure and composition while simultaneously allowing atomic resolution imaging at ambient pressure. The results show that 0.25-nm lattice fringes are directly visible for nanoparticles imaged at ambient pressure with gas path lengths up to 20 µm. Additionally, we quantitatively demonstrate that while the attainable contrast and resolution decrease with increasing pressure and gas path length, resolutions better than 0.2 nm should be accessible at ambient pressure with gas path lengths less than the 15 µm utilized for these experiments.

Triosmium clusters on a support: determination of structure by X-ray absorption spectroscopy and high-resolution microscopy.

The structures of small, robust metal clusters on a solid support were determined by a combination of spectroscopic and microscopic methods: extended X-ray absorption fine structure (EXAFS) spectroscopy, scanning transmission electron microscopy (STEM), and aberration-corrected STEM. The samples were synthesized from [Os(3) (CO)(12) ] on MgO powder to provide supported clusters intended to be triosmium. The results demonstrate that the supported clusters are robust in the absence of oxidants. Conventional high-angle annular dark-field (HAADF) STEM images demonstrate a high degree of uniformity of the clusters, with root-mean-square (rms) radii of 2.03±0.06 Å. The EXAFS OsOs coordination number of 2.1±0.4 confirms the presence of triosmium clusters on average and correspondingly determines an average rms cluster radius of 2.02±0.04 Å. The high-resolution STEM images show the individual Os atoms in the clusters, confirming the triangular structures of their frames and determining OsOs distances of 2.80±0.14 Å, matching the EXAFS value of 2.89±0.06 Å. IR and EXAFS spectra demonstrate the presence of CO ligands on the clusters. This set of techniques is recommended as optimal for detailed and reliable structural characterization of supported clusters.

Tantalum clusters supported on silica-alumina: influence of support composition and chemistry on cluster structure.

Small cationic tantalum clusters were prepared on the surfaces of SiO2, silica-aluminas, and gamma-Al2O3 supports by treating physisorbed pentabenzyltantalum at 523 K for 24 h in flowing H2. The rate of decomposition and the products formed in the decomposition of pentabenzyltantalum are dependent on the support composition. When the support was SiO2, the evolved products were mainly biphenyl and a small amount of toluene, indicating that the Ta-C bond in pentabenzyltantalum was activated. As the alumina content of the support increased, diphenylmethane, benzene, and ethylene were increasingly formed, and these products show that the activation of the C-C bonds linking the C atoms of methyl groups to the aromatic rings of the benzyl ligands was facilitated. Infrared spectra of the surface species and mass spectra of the effluents formed during the treatment show that the composition of the support had significant influence on the decomposition of pentabenzyltantalum, and the chemistry is inferred to be related to the electron-donor properties of the supports. Extended X-ray absorption fine structure (EXAFS) spectra recorded at the Ta LIII edge indicate the formation of clusters with a Ta-Ta first-shell coordination number of approximately 3, and images obtained by scanning transmission electron microscopy (STEM) confirm the presence of such small clusters. X-ray absorption near edge structure (XANES) data indicate that the formal oxidation state of the tantalum in the clusters decreased from approximately 3.0 to approximately 2.6 as the support was changed from SiO2 to silica-aluminas to gamma-Al2O3. The data suggest that the tantalum clusters were anchored to the supports via bridging O atoms. The EXAFS data show that the support composition had little influence on the cluster structure.