Effect of different gases on the sonochemical Cr(VI) reduction in the presence of citric acid.

The sonochemical (850 kHz) Cr(VI) reduction (0.30 mM, pH 2) in the presence of citric acid (Cit, 2 mM) was analyzed under different working atmospheres: reactor open to air without sparging (ROAWS), and Ar, O2, air and N2 sparging. Hydrogen peroxide formation in pure water at pH 2 and KI dosimetry were also measured. Zero-order kinetics was observed in all cases. A complete Cr(VI) reduction after 180 min insonation was obtained with the ROAWS and under Ar, while a lower Cr(VI) reduction efficiency was achieved under the other conditions. The Cr(VI) reduction and H2O2 formation rates followed the order ROAWS â‰… Ar > air â‰… O2 ≫ N2, while for KI dosimetry the order was ROAWS â‰« O2 â‰… air > Ar â‰« N2. This indicates that H2O2 formation rate is a better measure of the system reactivity for Cr(VI) reduction. For air, O2 and N2, once the sparging was stopped, Cr(VI) reduction rate increased up to approximately the same value obtained for the ROAWS, suggesting that the sparging decreased the generation of reactive species and, thus, the Cr(VI) reduction rate. Nitrate production was measured at low concentrations (micromolar range) in the ROAWS, air and N2 systems. Formic and acetic acids were detected as Cit degradation products. Reaction mechanisms were proposed. It can be concluded that the best condition for Cr(VI) removal is with the ROAWS because of a higher Cr(VI) reduction rate, no atmosphere control is required, and it is a less expensive system.

Iron-based nanoparticles prepared from yerba mate extract. Synthesis, characterization and use on chromium removal.

Iron-based nanoparticles were synthesized by a rapid method at room temperature using yerba mate (YM) extracts with FeCl3 in different proportions. Materials prepared from green tea (GT) extracts were also synthesized for comparison. These materials were thoroughly characterized by chemical analyses, XRD, magnetization, SEM-EDS, TEM-SAED, FTIR, UV-Vis, Raman, Mössbauer and XANES spectroscopies, and BET area analysis. It was concluded that the products are nonmagnetic iron complexes of the components of the extracts. The applicability of the materials for Cr(VI) (300 µM) removal from aqueous solutions at pH 3 using two Cr(VI):Fe molar ratios (MR), 1:3 and 1:0.5, has been tested. At Cr(VI):Fe MR = 1:3, the best YM materials gave complete Cr(VI) removal after two minutes of contact, similar to that obtained with commercial nanoscale zerovalent iron (N25), with dissolved Fe(II), and with a likewise prepared GT material. At a lower Cr(VI):Fe MR (1:0.5), although Cr(VI) removal was not complete after 20 min of reaction, the YM nanoparticles were more efficient than N25, GT nanoparticles and Fe(II) in solution. The results suggest that an optimal Cr(VI):Fe MR ratio could be reached when using the new YM nanoparticles, able to achieve a complete Cr(VI) reduction, and leaving very low Cr and Fe concentrations in the treated solutions. The rapid preparation of the nanoparticles would allow their use in removal of pollutants in soils and groundwater by direct injection of the mixture of precursors.

Sonochemical reduction of Cr(VI) in air in the presence of organic additives: What are the involved mechanistic pathways?

The sonochemical (850 kHz) reduction of Cr(VI) (0.3 mM, pH 2, reactor open to air) was analyzed in the presence of different additives. The effects on Cr(VI) reduction efficiency of added formic acid (FA, 10 mM), citric acid (Cit, 2 mM), ethylenediaminetetraacetic acid (EDTA, 1 mM), methanol (MeOH, 0.1 M), ethanol (EtOH, 0.1 M), 2-propanol (2-PrOH, 0.1 M), tert-butanol (t-BuOH, 0.1 M), phenol (PhOH, 2 mM) and sodium lauryl sulfate (SLS, 1 mM) have been evaluated in comparison with the system in the absence of additives. Complete Cr(VI) reduction was obtained only when using EDTA (at 120 min) and Cit (at 180 min). Cr(III) complexes with these compounds or with their degradation products were detected as final products. For EDTA, Cit, t-BuOH, FA and SLS, the Cr(VI) decay could be adjusted to a zero-order kinetics; in the cases of MeOH, EtOH and 2-PrOH, there was a deviation from the zero-order kinetics. The Cr(VI) conversion increased in the order SLS (very low) < no additive ≅ MeOH ≅ EtOH ≅ 2-PrOH < FA < t-BuOH < PhOH < Cit < EDTA. The role of EDTA and Cit in stabilizing intermediate Cr(V) peroxo compounds and enhancing their direct transformation into different Cr(III) species is considered a major factor in the acceleration of Cr(VI) reduction processes. Mechanistic pathways are proposed.

Monitoring of toxicity of As(V) solutions by AMPHITOX test without and with treatment with zerovalent iron nanoparticles.

Changes in toxicity of As(V) solutions from acute to chronic exposure have been evaluated by the AMPHITOX test. This test employs Rhinella arenarum, a widely distributed toad in Argentine areas. LOEC values were 6.37 and 1.88 mg L-1 for embryos and larvae, respectively, and serious sublethal effects have been observed. Toxicity of As(V) solutions has been also evaluated after treatment with zerovalent iron nanoparticles (nZVI). After 60 min of treatment with nZVI, As(V) removal was 77%, and neither lethal nor sublethal effects were observed. However, nZVI had to be eliminated before the bioassay because they caused adverse effects in both embryos and larvae. This work highlights the high sensitivity of R. arenarum to As(V), the relevance to assess toxicity on different periods of the lifecycle, and the need to expand exposure to As(V) to chronic times. The utility of the test for monitoring toxicity changes in As(V) solutions after nZVI treatment has been also shown.

Mechanistic Features of the TiO2 Heterogeneous Photocatalysis of Arsenic and Uranyl Nitrate in Aqueous Suspensions Studied by the Stopped-Flow Technique.

The dynamics of the transfer of electrons stored in TiO2 nanoparticles to As(III) , As(V) , and uranyl nitrate in water was investigated by using the stopped-flow technique. Suspensions of TiO2 nanoparticles with stored trapped electrons (etrap (-) ) were mixed with solutions of acceptor species to evaluate the reactivity by following the temporal evolution of etrap (-) by the decrease in the absorbance at λ=600 nm. The results indicate that As(V) and As(III) cannot be reduced by etrap (-) under the reaction conditions. In addition, it was observed that the presence of As(V) and As(III) strongly modified the reaction rate between O2 and etrap (-) : an increase in the rate was observed if As(V) was present and a decrease in the rate was observed in the presence of As(III) . In contrast with the As system, U(VI) was observed to react easily with etrap (-) and U(IV) formation was observed spectroscopically at λ=650 nm. The possible competence of U(VI) and NO3 (-) for their reduction by etrap (-) was analyzed. The inhibition of the U(VI) photocatalytic reduction by O2 could be attributed to the fast oxidation of U(V) and/or U(IV) .

Introducing Simple Detection of Bioavailable Arsenic at Rafaela (Santa Fe Province, Argentina) Using the ARSOlux Biosensor.

Numerous articles have reported the occurrence of arsenic in drinking water in Argentina, and the resulting health effects in severely affected regions of the country. Arsenic in drinking water in Argentina is largely naturally occurring due to elevated background content of the metalloid in volcanic sediments, although, in some regions, mining can contribute. While the origin of arsenic release has been discussed extensively, the problem of drinking water contamination has not yet been solved. One key step in progress towards mitigation of problems related with the consumption of As-containing water is the availability of simple detection tools. A chemical test kit and the ARSOlux biosensor were evaluated as simple analytical tools for field measurements of arsenic in the groundwater of Rafaela (Santa Fe, Argentina), and the results were compared with ICP-MS and HPLC-ICP-MS measurements. A survey of the groundwater chemistry was performed to evaluate possible interferences with the field tests. The results showed that the ARSOlux biosensor performed better than the chemical field test, that the predominant species of arsenic in the study area was arsenate and that arsenic concentration in the studied samples had a positive correlation with fluoride and vanadium, and a negative one with calcium and iron.

Application of the Stopped Flow Technique to the TiO2-Heterogeneous Photocatalysis of Hexavalent Chromium in Aqueous Suspensions: Comparison with O2 and H2O2 as Electron Acceptors.

The dynamics of the transfer of electrons stored in TiO2 nanoparticles to Cr(VI) in aqueous solution have been investigated using the stopped flow technique. TiO2 nanoparticles were previously irradiated under UV light in the presence of formic acid, and trapped electrons (e(trap)(-)) were made to react with Cr(VI) as acceptor species; other common acceptor species such as O2 and H2O2 were also tested. The temporal evolution of the number of trapped electrons was followed by the decrease in the absorbance at 600 nm, and the kinetics of the electron-transfer reaction was modeled. Additionally, the rate of formation of the surface complex between Cr(VI) and TiO2 was determined with the stopped flow technique by following the evolution of the absorbance at 400 nm of suspensions of nonirradiated TiO2 nanoparticles and Cr(VI) at different concentrations. An approximately quadratic relationship was observed between the maximum absorbance of the surface complex and the concentration of Cr(VI), suggesting that Cr(VI) adsorbs onto the TiO2 surface as dichromate. The kinetic analyses indicate that the electron transfer from TiO2 to Cr(VI) does not require the previous formation of the Cr(VI)-TiO2 surface complex, at least the complex detected here through the stopped flow experiments. When previously irradiated TiO2 was used to follow the evolution of the Cr(VI)-TiO2 complex, an inhibition of the formation of the complex was observed, which can be related to the TiO2 deactivation caused by Cr(III) deposition.

Evidence on dye clustering in the sensitization of TiO2 by aluminum phthalocyanine.

As previous studies have shown, the photocatalytic reduction of Cr(VI) to Cr(III) in the presence of 4-chlorophenol can be carried out efficiently under visible irradiation using TiO2 modified with hydroxoaluminum-tricarboxymonoamide phthalocyanine (AlTCPc) in spite of the high aggregation tendency of the dye. In the present work, photocurrent and absorption spectra of AlTCPc modified TiO2 films are studied together with absorption and fluorescence of the dye in solution as a function of the concentration of the dye to clarify (a) the role of aggregates and the nature of the species responsible for electron injection into the semiconductor and (b) the reasons why, as reported earlier, the photocatalytic activity is nearly independent of dye loading at constant TiO2 mass. Results are consistent with the presence of AlTCPc clusters with similar properties both on the TiO2 surface and in H2O-DMSO solution. The actual photoactive species is the monomeric dye electronically coupled to the semiconductor. Monomer concentration depends only slightly on AlTCPc analytical concentration, in a way similar to surfactant monomers in micellar equilibrium, thus explaining the independence of photocatalytic activity on dye concentration.

Photoreduction of Cr(VI) using hydroxoaluminiumtricarboxymonoamide phthalocyanine adsorbed on TiO2.

Hydroxoaluminiumtricarboxymonoamide phthalocyanine (AlTCPc) adsorbed at different loadings on TiO(2) Degussa P-25 was tested for Cr(vi) photocatalytic reduction under visible irradiation in the presence of 4-chlorophenol (4-CP) as sacrificial donor. A rapid reaction takes place in spite of the presumable aggregation of the dye on the TiO(2) surface. The removal of Cr(vi) is fairly negligible under visible-light irradiation, either without photocatalyst or in the presence of bare TiO(2). The fast capture of conduction band electrons by Cr(vi), which forms a surface complex with TiO(2), inhibits the formation of reactive oxygen species in the reductive pathway. This fact and the easier oxidation of 4-CP as compared to AlTCPc hinder the photobleaching of the dye and make feasible Cr(vi) reduction under visible irradiation. The consumption of Cr(vi) follows a pseudo-first order kinetics; the decay constant depends, in the studied range, on the photocatalyst mass, but it is barely affected by dye loading. The presence of 4-CP is essential, but its concentration has no effect on the Cr(vi) decay rate. Oxidation products of 4-CP, such as hydroquinone, catechol or benzoquinone, are not observed. Direct evidence of the one-electron reduction of Cr(vi) to Cr(v) was obtained by EPR spectroscopy using citric acid as Cr(v) trapping agent. In this case, disappearance of Cr(v) also follows a first order decay, but conduction band electrons do not seem to be involved. The fact that oxidation products of 4-CP are not observed is consistent with the fast dark removal of reaction intermediates by Cr(v), proved by EPR.