RESUMO
Cooperativity among spin centres has long been the royal road in spin crossover (SCO) research to impose magnetic bistability in terms of thermal hysteresis. In this work we access magnetic multi-inert states of the iron(III) compound {FeL2[B(Ph)4]} ≡ FeB at low temperature, in addition to thermal bistability. The packing of the low-spin and high-spin forms of crystalline FeB differs only marginally what ultimately leads to structural conservatism. This indicates that the SCO-immanent breathing of the complex cation is almost fully compensated by the anion matrix. The unique cooling rate dependence of the residual low-temperature magnetisation in FeB unveils continuous switching between the trapped high-spin (ON) and the relaxed low-spin state (OFF). The macroscopic ratio of the spin states (ON:OFF) can be adjusted as a simple function of the cooling rate. That is, cooperative spin crossover can be the source of bistable and multi-inert system states in the very same material.
RESUMO
Graphene and its derivatives have emerged as potential materials for several technological applications including sunlight-driven water splitting reactions. This review critically addresses the latest achievements concerning the use of graphene as a player in the design of hybrid-photoelectrodes for photoelectrochemical cells. Insights about the charge carrier dynamics of graphene-based photocatalysts which include metal oxides and non-metal oxide semiconductors are also discussed. The concepts underpinning the continued progress in the field of graphene/photoelectrodes, including different graphene structures, architecture as well as the possible mechanisms for hydrogen and oxygen reactions are also presented. Despite several reports having demonstrated the potential of graphene-based photocatalysts, the achieved performance remains far from the targeted benchmark efficiency for commercial application. This review also highlights the challenges and opportunities related to graphene application in photoelectrochemical cells for future directions in the field.
RESUMO
Graphene quantum dots (GQDs) have emerged as a new group of quantum-confined semiconductors in recent years, with possible applications as light absorbers, luminescent labels, electrocatalysts, and photoelectrodes for photoelectrochemical water splitting. However, their semiconductor characteristics, such as the effective band gap, majority carrier type, and photochemistry, are obscured by defects in this material. Herein, we use surface photovoltage spectroscopy (SPS) in combination with photoelectrochemical measurements to determine the parameters that are essential to the use of GQDs as next-generation semiconductor devices and photocatalysts. Our results show that ordered GQDs (1-6 nm) behave as p-type semiconductors, based on the positive photovoltage in the SPS measurements on Al, Au, and fluorine-doped tin oxide substrates, and generate mobile charge carriers under excitation of defect states at 1.80 eV and under band gap excitation at 2.62 eV. Chemical reduction with hydrazine removes some defects and increases the effective band gap to 2.92 eV. SPS measurements in the presence of sacrificial electron donor and acceptors show that photochemical charge carriers can be extracted and promote redox reactions. A reduced GQDs photocathode supports an unprecedented photocurrent of 50 µA cm-2 using K3Fe(CN)6 as sacrificial electron acceptor. Additionally, while pristine GQDs do not photoreduce protons under visible light, hydrazine-treated GQDs generate H2 from aqueous methanol under visible and UV light (0.04% quantum efficiency at 375 nm) without added co-catalysts. These findings are relevant to the use of GQDs in photochemical and photovoltaic energy-conversion systems.
RESUMO
Surface photovoltage spectroscopy (SPS) is used to measure the photopotential across a Ru-SrTiO3:Rh/BiVO4 particle tandem overall water splitting photocatalyst. The tandem is synthesized from Ru-modified SrTiO3:Rh nanocrystals and BiVO4 microcrystals by electrostatic assembly followed by thermal annealing. It splits water into H2 and O2 with an apparent quantum efficiency of 1.29% at 435 nm and a solar to hydrogen conversion efficiency of 0.028%. According to SPS, a photovoltage develops above 2.20 eV, the effective band gap of the tandem, and reaches its maximal value of -2.45 V at 435 nm (2.44 mW cm-2), which corresponds to 96% of the theoretical limit of the photocatalyst film on the fluorine-doped tin-oxide-coated glass (FTO) substrate. Charge separation is 82% reversible with 18% of charge carriers being trapped in defect states. The unusually strong light intensity dependence of the photovoltage (1.16 V per decade) is attributed to depletion layer changes inside of the BiVO4 microcrystals. These findings promote the understanding of solar energy conversion with inorganic particle photocatalysts.