RESUMO
A high consumption of solid fats is linked to increased inflammation and a risk of cardiovascular diseases. Hence, in recent years, there has been increasing interest in the development of oleogels as a fat substitute in food products. Oleogels are edible gels that contain a large amount of liquid oils entrapped in a 3D network and that can potentially be applied to spreads, bakery goods, meat, and dairy products in order to lower their saturated fat content while maintaining a desirable food texture and mouthfeel. In this work, alginate cryogels were studied as templates for three different edible oils in the process of oleogel formation. Two different freezing regimes to obtain cryogels were employed in order to evaluate better the textural and morphological capabilities of cryogels to adsorb and retain edible oils. It was shown that rapid freezing in liquid nitrogen produces alginate cryogels with a lower density, higher porosity, and a greater ability to adsorb the tested oils. The highest uptake and holding oil capacity was achieved for olive oil, which reached a value of 792% and 82%, respectively. The best chewiness was found for an oleogel containing olive oil, whereas oleogels with the other two tested oils showed better springiness. Hence, the results presented in this work demonstrated that alginate-based cryogels can be effectively used as templates for oleogels and potentially find applications in the food industry.
RESUMO
In this research, the pectin monoliths were prepared via the sol-gel process through different routes of crosslinking and additional freeze-drying. The crosslinking reaction was induced by the use of calcium ions in aqueous solutions and in alcohol/water solutions. The resulting pectin monoliths obtained by freeze-drying were macroporous with open cells, limited specific surface area, moderate mechanical stability and moderate biodegradation rate. The presence of alcohol in crosslinking solution significantly changed the morphology of final pectin monoliths, which was evidenced by the reduction of their pore size for one order. The specific surface area of pectin monoliths obtained through the calcium-water-alcohol route was 25.7 m2/g, the Young compressive modulus was 0.52 MPa, and the biodegradation rate was 45% after 30 days of immersion in compost media. Considering that pectin can be obtained from food waste, and its physical properties could be tailored by different crosslinking routes, the pectin monoliths could find wide application in the pharmaceutical, agricultural, medical and food industries, providing sustainable development concepts.
RESUMO
Pectin is a natural biopolymer with broad applications in the food industry and it is suitable to prepare edible films to prolong food shelf-life. However, the main limitation of pectin-based films is their poor mechanical and barrier properties. Zeolite Y is a hydrophobic clay that can be used as film reinforcement material to improve its physicochemical and mechanical properties. In this work, the influence of high methoxyl citrus and apple pectin on physicochemical properties of biopolymer films modified with zeolite Y (0.05-0.2 wt%) was investigated. The films were characterized by FTIR, TGA, WAXD, mechanical analysis, and water vapor permeability analysis, and a potential film application is presented. The WAXD and FTIR analysis demonstrated that the strongest interaction between pectin chains and zeolite Y occurred when citrus high methylated pectin was used. Adding 0.2 wt% of zeolite Y into citrus high methylated pectin matrix enhanced the tensile strength by 66%, thermal stability by 13%, and water vapor barrier by 54%. In addition, fruit shelf-life test was performed, where strawberries were sealed in film. It was shown that sealed strawberries maintained a better color and healthy appearance than the control treatment after 7 days at 10 °C. This study enabled the development of biocomposite films with improved properties for potential application in food packaging.