RESUMO
The tannin extract of Cissus dinklagei was used in the preparation of a 3 % paraformaldehyde resin for the manufacture of particleboard. This tannin is of the procyanidin type associated with furan residues. The modulus of elasticity of the resin obtained after the thermomechanical analysis is 3825 MPa. The TGA performed on the panels obtained shows three degradation zones with a thermal stability zone between 74 and 210 °C. These panels have good thermomechanical properties. The values of the best density, internal bond, modulus of elasticity in flexion (MOE) and resistance to flexion (MOR) are respectively 658 kg/m3; 0.52 MPa; 2035.4 MPa; 16.3 MPa. These results classify this panel for generalinterior construction and furniture uses according to the NF EN 312 standard.
RESUMO
Tropical Triumfetta cordifolia (TC) fibre extracted from the equatorial region of Cameroon has been characterized as a potential fibre for textiles. An investigation of extraction parameters to soften this fibre is crucial to use it as a biobased material in the spinning process. To obtain textile quality fibres, 34 sodium hydroxide extraction tests were carried out to study the effect of extraction conditions on its characteristics. Thus, three levels of concentrations (0.5, 1.0 and 1.5 wt%), temperatures (80, 100 and 120 °C) and durations (120, 180 and 240min) were used for extraction by cooking, and at room temperature, durations of 120, 150 or 180 min with three concentrations (2.5, 3.0 and 3.5 wt%) were considered. Only 6 combinations produced fibres that were clear and soft to the touch, without defects (corrugations, stuck fibres) and without residual bark epidermis at the macroscopic scale. For these fibres, the dissolution of non-cellulosic substances, morphological, physical, thermal and mechanical properties depended on the austerity of the alkaline retting. Under mild conditions, the SEM surfaces of the fibres showed large residues of the middle lamella, which made the lignin content (10 wt%) and hydrophilic function higher. Under medium conditions, the fibre surfaces were clean and slightly wrinkled (at 80 °C; 120min). Under severe conditions, heterogeneous transverse shrinkage and wrinkling were observed and accompanied by cellulose degradation (39 wt%) with a significant reduction in tenacity at 16cN/tex. The medium extraction conditions were considered more effective, and their fibres showed cellulose content up to 49 wt%, density up to 1.39 g cm-3, "Fickian" moisture absorption kinetics with saturation up to 11 wt%, thermal stability up to 237 °C, Young's modulus up to 3.7 GPa, tensile strength up to 113 MPa and tenacity up to 40cN/tex. These new results were compared with lignocellulosic textile fibres in the literature, showing similarity with banana, sisal and jute fibres.