Sodium magnesium amidoborane: the first mixed-metal amidoborane.

The first example of a mixed-metal amidoborane Na(2)Mg(NH(2)BH(3))(4) has been successfully synthesized. It forms an ordered arrangement in cation coordinations, i.e., Mg(2+) bonds solely to N(-) and Na(+) coordinates only with BH(3). Compared to ammonia borane and monometallic amidoboranes, Na(2)Mg(NH(2)BH(3))(4) can release 8.4 wt% pure hydrogen with significantly less toxic gases.

Size effects on the hydrogen storage properties of nanoscaffolded Li3BN2H8.

The use of Li3BN2H8 complex hydride as a practical hydrogen storage material is limited by its high desorption temperature and poor reversibility. While certain catalysts have been shown to decrease the dehydrogenation temperature, no significant improvement in reversibility has been reported thus far. In this study, we demonstrated that tuning the particle size to the nanometer scale by infiltration into nanoporous carbon scaffolds leads to dramatic improvements in the reversibility of Li3BN2H8. Possible changes in the dehydrogenation path were also observed in the nanoscaffolded hydride.

Improved hydrogen release from LiB0.33N0.67H2.67 with noble metal additions.

The hydrogen release behavior of the quaternary hydride LiB(0.33)N(0.67)H(2.67) has been successfully improved through the incorporation of small quantities of noble metal. Adding 5 wt % Pd either as Pd metal particles or as PdCl(2) reduced the temperature T(1/2) corresponding to the midpoint of the hydrogen release reaction by DeltaT(1/2) = -43 degrees C and -76 degrees C, respectively. PtCl(2) and Pt nanoparticles supported on a Vulcan carbon substrate proved to be even more effective, with DeltaT(1/2) = -90 degrees C. The amount of NH(3) released during dehydrogenation is reduced compared to that from additive-free material, and, more importantly, at temperatures below 210 degrees C hydrogen is released with no detectable NH(3). In contrast to additive-free LiB(0.33)N(0.67)H(2.67), which melts completely above 190 degrees C and releases hydrogen from the liquid state only above approximately 250 degrees C, hydrogen release from LiB(0.33)N(0.67)H(2.67) + 5 wt % Pt/Vulcan carbon is accompanied by partial melting plus a cascade through a series of solid intermediate phases. Calorimetric measurements indicate that both additive-free and Pt-added LiB(0.33)N(0.67)H(2.67) release hydrogen exothermically, and hence the reverse reaction is thermodynamically unfavorable. By exposing partially dehydrogenated samples to high H(2) pressures at modest temperatures, fractional hydrogen uptake (roughly 15% of the released hydrogen) has been achieved. The mechanism by which noble metals promote hydrogen release is not known, but the behavior is consistent with that expected for a catalyst, including a large effect with small additions and saturation of the effect at low concentration.

Hydrogen release from mixtures of lithium borohydride and lithium amide: a phase diagram study.

We recently reported the synthesis of a new quaternary hydride in the lithium-boron-nitrogen-hydrogen quaternary phase diagram with the approximate composition LiB0.33N0.67H2.67 having a theoretical hydrogen content of 11.9 wt %. This new compound forms by the reaction of appropriate amounts of lithium amide (LiNH2) and lithium borohydride (LiBH4) and releases greater than 10 wt % hydrogen when heated. A small amount of ammonia, 2-3 mol % of the generated gas, is also released. We now report a study of hydrogen and ammonia release from the series of reactant mixtures (LiNH2)x(LiBH4)1-x, where x=0.667 corresponds to the composition LiB0.33N0.67H2.67. We measured hydrogen and ammonia release amounts as a function of composition and found that maximum hydrogen and minimum ammonia release do occur for x=0.667. We also present evidence for an additional new quaternary phase and for two possibly metastable phases in this system.

Hydrogen desorption exceeding ten weight percent from the new quaternary hydride Li3BN2H8.

Mobile applications of hydrogen power have long demanded new solid hydride materials with large hydrogen storage capacities. We report synthesis of a new quaternary hydride having the approximate composition Li(3)BN(2)H(8) with 11.9 wt % theoretical hydrogen capacity. It forms by reacting LiNH(2) and LiBH(4) powders in a 2:1 molar ratio either by ball milling or by heating the mixed powders above 95 degrees C. This new quaternary hydride melts at approximately 190 degrees C and releases > or =10 wt % hydrogen above approximately 250 degrees C. A small amount of ammonia (2-3 mol % of the generated gas) is released simultaneously. Preliminary calorimetric measurements suggest that hydrogen release is exothermic and, hence, not easily reversible.