Fatigue fracture of a forged cobalt-chromium-molybdenum femoral component inserted with cement. A report of ten cases.

Ten patients who had had a total hip replacement with a forged cobalt-chromium-molybdenum femoral prosthesis (Precoat or Precoat Plus) inserted with cement were seen with a fatigue fracture of the stem an average of fifty months (range, nineteen to seventy-four months) postoperatively. The average age of the patients was sixty-one years (range, forty-three to seventy-three years), and the average weight was ninety-six kilograms (range, seventy to 130 kilograms). Eight patients had had a primary total hip replacement, and two had had a revision; all of the acetabular components had been inserted without cement. Radiographs that had been made before the fracture were available for four of the eight hips that had had a primary replacement; all four had radiographic evidence of debonding of the cement mantle from the proximal end of the stem. This probably caused exaggerated cantilever bending stresses on the proximal aspect of the stem as the distal end of the stem was well fixed. The radiographs of both hips that had had a revision demonstrated a non-union of the greater trochanter, which had resulted in separation at the cement-bone interface at the proximal portion of the femur before the fracture. Scanning electron micrographs of five of the ten fractured prostheses demonstrated a fatigue fracture that began near the anterolateral corner of the prosthesis, through characters that had been etched on the implant with a laser. Metallurgical analysis indicated subsurface voids or inclusions, or both, immediately under the region that had been etched. This finding is consistent with thermal changes to the microstructure of the alloy that probably caused a focal reduction in the material strength. A high proportion (seven) of the ten stems had a poor cement mantle. Also, of the seven small stems that were used, six had been implanted in patients who weighed more than eighty kilograms, so there was relative undersizing of the prostheses. Early debonding of the proximal end of a Precoat femoral prosthesis from the cement mantle may occur as a result of a thin cement mantle, leading to loosening and possibly to early fatigue fracture of the stem if the distal portion of the stem remains solidly fixed in the distal portion of the cement column. On the basis of our experience, we recommend that patients who have radiographic evidence of a debonded Precoat femoral component should be informed of the risk of fatigue fracture of the stem and be followed closely even though there may be no symptoms of loosening of the femoral component.

Aspirin-sulfinpyrazone in prophylaxis of deep venous thrombosis in total hip replacement.

In postoperative hip arthroplasty patients, treatment with aspirin and sulfinpyrazone resulted in a statistically significant reduction of venographically diagnosed thrombi in the proximal veins of the leg. This reduction was most apparent in thrombi that involved the iliac vein. When compared with their placebo-treated counterparts, female patients who received the active treatment experienced a statistically significant 75% reduction of thrombosis, compared with a 32% reduction for men that was not statistically significant. There were no serious adverse effects. Factors were identified that may influence the result of drug prophylaxis trials in deep-vein thrombosis.

The limited utility of fibrinogen I 125 leg scanning.

Using venography as the reference procedure, this study examined the utility of fibrinogen I 125 scanning for the detection or demonstration of deep venous thrombosis. The results demonstrate the inability of leg scanning to detect accurately the presence or absence of thrombi in the deep venous system. Most striking was the lack of sensitivity of this procedure in areas where the propensity for embolization is greatest. Sensitivity is extremely low in the anatomic areas where leg scanning demonstrates reasonable specificity. The results are nearly identical in the extremity not operated upon. The validity of all prior studies relying heavily or exclusively on 125I leg scans to determine the presence or absence of thrombi must be critically reassessed.