Superconductivity (SC) was experimentally observed for the first time in antimony polyhydride. The diamond anvil cell combined with a laser heating system was used to synthesize the antimony polyhydride sample at high pressure and high temperature. In-situ high pressure transport measurements as a function of temperature with an applied magnetic field were performed to study the SC properties. It was found that the antimony polyhydride samples show superconducting transition with critical temperature T c 116 K at 184 GPa. The investigation of SC at magnetic field revealed the superconducting coherent length of â¼40 Å based on the Ginzburg Landau (GL) equation. Antimony polyhydride superconductor has the second highest T c in addition to sulfur hydride among the polyhydrides of elements from main groups IIIA to VIIA in the periodic table.
RESUMO
Searching for superconductivity with Tc near room temperature is of great interest both for fundamental science & many potential applications. Here we report the experimental discovery of superconductivity with maximum critical temperature (Tc) above 210 K in calcium superhydrides, the new alkali earth hydrides experimentally showing superconductivity above 200 K in addition to sulfur hydride & rare-earth hydride system. The materials are synthesized at the synergetic conditions of 160~190 GPa and ~2000 K using diamond anvil cell combined with in-situ laser heating technique. The superconductivity was studied through in-situ high pressure electric conductance measurements in an applied magnetic field for the sample quenched from high temperature while maintained at high pressures. The upper critical field Hc(0) was estimated to be ~268 T while the GL coherent length is ~11 Å. The in-situ synchrotron X-ray diffraction measurements suggest that the synthesized calcium hydrides are primarily composed of CaH6 while there may also exist other calcium hydrides with different hydrogen contents.