In vitro biocompatibility of modified potassium fluorrichterite and potassium fluorrichterite-fluorapatite glass-ceramics.

Potassium fluorrichterite (KNaCaMg(5)Si(8)O(22)F(2)) glass-ceramics were modified by either increasing the concentration of calcium in the glass (GC5), or by the addition of P(2)O(5) to produce potassium fluorrichterite-fluorapatite (GP2). The solubility of the stoichiometric composition (GST), GC5 and GP2 were measured using the standard test described in ISO 6872:1995 (Dental Ceramics). Ion release profiles were determined for Si, Ca, Mg, Na, K and P using inductively coupled plasma mass spectrometry and fluoride ion (F(-)) concentration was measured using an ion-selective electrode. The cytotoxicity of all compositions was assessed using cultured rat osteosarcoma cells (ROS, 17/2.8). Cell response was qualitatively assessed using scanning electron microscopy (SEM) and quantitatively using the Alamar blue assay. GST was the least soluble and also released the lowest concentration of ions following immersion in water. Of the modified compositions, GC5 demonstrated intermediate solubility but the greatest ion release while GP2 exhibited the highest solubility. This was most likely due to GC5 having the greatest proportion of residual glass following crystallisation. The mass loss exhibited by GP2 may have been due in part to the partial disintegration of the surface of specimens during solubility testing. SEM demonstrated that all compositions supported the growth of healthy ROS cells on their surfaces, and this data was further supported by the quantitative Alamar blue assay.

High throughput methodology for synthesis, screening, and optimization of solid state lithium ion electrolytes.

A study of the lithium ion conductor Li(3x)La(2/3-x)TiO(3) solid solution and the surrounding composition space was carried out using a high throughput physical vapor deposition system. An optimum total ionic conductivity value of 5.45 × 10(-4) S cm(-1) was obtained for the composition Li(0.17)La(0.29)Ti(0.54) (Li(3x)La(2/3-x)TiO(3)x = 0.11). This optimum value was calculated using an artificial neural network model based on the empirical data. Due to the large scale of the data set produced and the complexity of synthesis, informatics tools were required to analyze the data. Partition analysis was carried out to determine the synthetic parameters of importance and their threshold values. Multivariate curve resolution and principal component analysis were applied to the diffraction data set. This analysis enabled the construction of phase distribution diagrams, illustrating both the phases obtained and the compositional zones in which they occur. The synthetic technique presented has significant advantages over other thin film and bulk methodologies, in terms of both the compositional range covered and the nature of the materials produced.

Prediction of osteoconductive activity of modified potassium fluorrichterite glass-ceramics by immersion in simulated body fluid.

Potassium fluorrichterite (KNaCaMg(5)Si(8)O(22)F(2)) glass-ceramics were modified by either increasing the concentration of calcium (GC5) or by the addition of P(2)O(5) (GP2). The stoichiometric composition (GST), GC5 and GP2 were soaked in simulated body fluid (SBF) along with 45S5-type bioglass as a control. After immersion, surface analyses were performed using thin-film X-ray diffraction (TF-XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and Fourier-transform infrared (reflection) spectroscopy (FT-IR). All compositions showed the formation of a calcium phosphate rich surface layer in SBF; GST, GP2 and the bioglass control within 7 days of immersion and GC5 after 14 days. It was concluded that all compositions were likely to be osteoconductive in vivo, with GP2 providing the best performance in terms of the combination of rapid formation of the surface layer and superior mechanical properties. This glass-ceramic system has potential as a load bearing bioceramic for fabrication of medical devices intended for skeletal tissue repair.