Effect of Self-etch Adhesives on Self-sealing Ability of High-Copper Amalgams.

STATEMENT OF THE PROBLEM: Similar to conventional amalgam, high-copper amalgam alloy may also undergo corrosion, but it takes longer time for the resulting products to reduce microleakage by sealing the micro-gap at the tooth/amalgam interface. PURPOSE: The aim of this study was to evaluate the effect of self-etch adhesives with different pH levels on the interfacial corrosion behavior of high-copper amalgam restoration and its induction potential for self-sealing ability of the micro-gap in the early hours after setting by means of Electro-Chemical Tests (ECTs). MATERIALS AND METHOD: Thirty cylindrical cavities of 4.5mm x 4.7mm were prepared on intact bicuspids. The samples were divided into five main groups of application of Adhesive Resin (AR)/ liner/ None (No), on the cavity floor. The first main group was left without an AR/ liner (No). In the other main groups, the types of AR/ liner used were I-Bond (IB), Clearfil S3 (S3), Single Bond (SB) and Varnish (V). Each main group (n=6) was divided into two subgroups (n=3) according to the types of the amalgams used, either admixed ANA 2000 (ANA) or spherical Tytin (Tyt). The ECTs, Open Circuit Potential (OCP), and the Linear Polarization Resistance (LPR) for each sample were performed and measured 48 hours after the completion of the samples. RESULTS: The Tyt-No and Tyt-IB samples showed the highest and lowest OCP values respectively. In LPR tests, the Rp values of ANA-V and Tyt-V were the highest (lowest corrosion rate) and contrarily, the ANA-IB and Tyt-IB samples, with the lowest pH levels, represented the lowest Rp values (highest corrosion rates). CONCLUSION: Some self-etch adhesives may increase interfacial corrosion potential and self-sealing ability of high-copper amalgams.

Effect of fluoride on nickel-titanium and stainless steel orthodontic archwires: an in-vitro study.

OBJECTIVES: The commonly used Nickel-Titanium (NiTi) archwires in orthodontic treatment are often exposed to fluoride-containing mouthwashes. The aim of this in-vitro study was to evaluate and compare the corrosion resistance of three commercially available NiTi archwires exposed to 0.05 wt% and 0.2 wt% fluoride mouthwashes. MATERIALS AND METHODS: Three different types of NiTi archwires, 0.016″ in diameter, from Dentaurum, Global, and GAC, and a stainless steel archwire from Dentaurum were examined to assess their corrosion resistance in Fusayama-Meyer artificial saliva and in two other artificial saliva containing 0.05 wt% and 0.2 wt% sodium fluoride (NaF). After the primary setup of wires, they were tested by potentiodynamic and potentiostatic polarization and corrosion potential/time analyses. Their surfaces were evaluated using a scanning electronic microscope (SEM). RESULTS: The results showed that all the wires were passive in artificial saliva. In contrast, by adding fluoride ions to the solution, the decrease in the archwires' corrosion resistance was in direct proportion to the increase in fluoride concentration. CONCLUSION: The NiTi wires experienced deterioration of their corrosion properties under the effect of fluoride but not as much as the stainless steel archwires.