Mesoporous Silica MCM-41 from Fly Ash as a Support of Bimetallic Cu/Mn Catalysts for Toluene Combustion.

The main outcome of this research was to demonstrate the opportunity to obtain a stable and well-ordered structure of MCM-41 synthesized from fly ash. A series of bimetallic (Cu/Mn) catalysts supported at MCM-41 were prepared via grinding method and investigated in catalytic toluene combustion reaction to show the material's potential application. It was proved, that the Cu/Mn ratio had a crucial effect on the catalytic activity of prepared materials. The best catalytic performance was achieved with sample Cu/Mn(2.5/2.5), for which the temperature of 50% toluene conversion was found to be 300 °C. This value remains in line with the literature reports, for which comparable catalytic activity was attained for 3-fold higher metal loadings. Time-on-stream experiment proved the thermal stability of the investigated catalyst Cu/Mn(2.5/2.5). The obtained results bring a valuable background in the field of fly ash utilization, where fly ash-derived MCM-41 can be considered as efficient and stable support for dispersion of active phase for catalyst preparation.

Decarbonatization of Energy Sector by CO2 Sequestration in Waste Incineration Fly Ash and Its Utilization as Raw Material for Alkali Activation.

In this study, municipal solid waste incineration (MSWI) fly ash was subjected to mineral carbonation with the aim of investigating CO2 sequestration in waste material. The conducted study follows the trend of searching for alternatives to natural mineral materials with the ability to sequestrate CO2. The mineral carbonation of MSWI fly ash allowed for the storage of up to 0.25 mmol CO2 g-1. Next, both carbonated and uncarbonated MSWI fly ashes were activated using an alkaline activation method by means of two different activation agents, namely potassium hydroxide and potassium silicate or sodium hydroxide and sodium silicate. Mineral carbonation caused a drop in the compressive strength of alkali-activated materials, probably due to the formation of sodium and/or potassium carbonates. The maximum compressive strength obtained was 3.93 MPa after 28 days for uncarbonated fly ash activated using 8 mol dm-3 KOH and potassium hydroxide (ratio 3:1). The relative ratio of hydroxide:silicate also influenced the mechanical properties of the materials. Both carbonated and uncarbonated fly ashes, as well as their alkali-activated derivatives, were characterized in detail by means of XRD, XRF, and FTIR. Both uncarbonated and carbonated fly ashes were subjected to TG analysis. The obtained results have proved the importance of further research in terms of high-calcium fly ash (HCFA) utilization.

Restoration of soils contaminated with PAHs by the mixture of zeolite composites mixed with exogenous organic matter and mineral salts.

The major cause of soil degradation (contamination, erosion, compaction) is closely linked to agriculture, i.e., unsustainable agriculture practices, which are reflected in the depletion of the soil organic carbon pool, loss in soil biodiversity, and reduction of C sink capacity in soils. Therefore, the agricultural practice of applying carbon-rich materials into the soil is an attractive solution for climate change mitigation and soil ecosystem sustainability. The paper aimed to evaluate the effectiveness of the addition of organic-mineral mixtures to the mineral salts (NPK), including the exogenous organic matter (lignite) mixed with zeolite-carbon (NaX-C) or zeolite-vermiculite (NaX-Ver) composites in the restoration of soils contaminated with PAHs. The addition of zeolite composites to fertilizer resulted in a significant reduction in soil PAH levels and a corresponding reduction in plant tissue content, without compromising yields, compared to the control and separate application of NPK. A Significant correlation between PAHs and pHH2O, pHKCl, EC and dehydrogenase activity (DhA) was found in soils. The addition of zeolite composites with lignite significantly reduced the content of PAHs in straws, especially following the application of NaX-C. However, in the case of grains, the highest percentage reduction in comparison to NPK was observed for the highest dose of NaX-Ver.

Zeolite Composite Materials from Fly Ash: An Assessment of Physicochemical and Adsorption Properties.

Waste fly ash, with both low (with the addition of vermiculite) and high contents of unburned coal, were subjected to hydrothermal syntheses aiming to obtain zeolite composite materials-zeolite + vermiculite (NaX-Ver) and zeolite + unburned carbon (NaX-C). The composites were compared with parent zeolite obtained from waste fly ash with a low content of unburned carbon (NaX-FA). In this study, the physicochemical characteristics of the obtained materials were evaluated. The potential application of the investigated zeolites for the adsorption of ammonium ions from aqueous solutions was determined. Composite NaX-Ver and parent zeolite NaX-FA were characterized by comparable adsorption capacities toward ammonium ions of 38.46 and 40.00 mg (NH4+) g-1, respectively. The nearly 2-fold lower adsorption capacity of composite NaX-C (21.05 mg (NH4+) g-1) was probably a result of the lower availability of ion exchange sites within the material. Adsorbents were also regenerated using 1 M NaCl solution at a pH of 10 and subjected to 3 cycles of adsorption-desorption experiments, which proved only a small reduction in adsorption properties. This study follows the current trend of waste utilization (fly ash) and the removal of pollutants from aqueous solutions with respect to their reuse, which remains in line with the goals of the circular economy.

Tomato green waste biochars as sustainable trivalent chromium sorbents.

Chromium removal from aqueous solutions has gained attention due to its hazardous impact on life organisms. In the present study, sorption processes were performed to examine the opportunity to apply biochar derived from waste tomato leaves and stems for Cr(III) ion removal. Biochars were produced through pyrolysis in a wide range of temperature (250-800 °C). The obtained biochars were investigated in detail by means of ultimate and proximate analyses, pH point of zero charge, FT-IR, scanning electron microscopy, and mercury porosimetry. Biochars are characterized by high amount of ash varying from 23 to 44% and as a result high pHpzc values of about 13. It was proven that increasing pyrolysis temperature positively affected sorption of Cr(III) ions. Mineral matter in the biochars plays a crucial role in the removal of Cr(III) ions from aqueous solution mainly due to their precipitation. The sorption capacity of biochar produced at 800 °C was 169.5 mg g-1, whereas at 250 °C only 62.2 mg g-1. It was found that biochar can be reused in sorption process after desorption using 0.1 M HCl, while the sorption capacity decreased 4-fold.