Fracture Resistance and Microleakage around Direct Restorations in High C-Factor Cavities.

The aim of this research was to evaluate the mechanical impact of different direct restorations in terms of fracture resistance, and subsequent fracture pattern, in occlusal high C-factor cavities. Furthermore, the adaptation of different direct restorations in the form of gap formation was also evaluated. Seventy-two intact mandibular molars were collected and randomly distributed into three groups (n = 24). Class I occlusal cavities with standardized dimensions were prepared in all specimens. After adhesive treatment, the cavities were restored with direct restorations utilizing three different materials. Group 1: layered conventional packable resin composite (Filtek Ultimate), Group 2: bulk-fill resin composite (SDR), Group 3: bulk-fill short fibre-reinforced composite (SFRC; everX Posterior) covered with packable composite occlusally. Half of the restored specimens underwent static load-to fracture testing (n = 12/group), while the rest underwent sectioning and staining for microleakage evaluation and gap formation analysis. Fracture patterns were evaluated visually among the mechanically tested specimens. The layered composite restoration (Group 1) showed significantly lower fracture resistance compared to the bulk fill groups (Group 2, p = 0.005, Group 3, p = 0.008), while there was no difference in fracture resistance between the other groups. In terms of gap formation values, the layered composite restoration (Group 1) produced significantly higher gap formation compared to the bulk-fill groups (Group 2, p = 0.000, Group 3, p = 0.000). Regarding the fracture pattern, SFRC (Group 3) produced the highest number, while SDR (Group 2) produced the lowest number of repairable fractures. The use of bulk-fill resin composite (fibre or non-fibre-reinforced) for occlusal direct restorations in high C-factor cavities showed promising achievements regarding both fracture resistance and microleakage. Furthermore, the use of short fibre-reinforced bulk-fill composite can also improve the fracture pattern of the restoration-tooth unit. Bulk-fill materials provide a simple and effective solution for restoring and reinforcing high C-factor occlusal cavities.

Fatigue performance of endodontically treated molars restored with different dentin replacement materials.

OBJECTIVES: The aim was to investigate the fatigue performance of endodontically treated (ET) molars restored by various dentin-replacing materials and material configurations. Moreover, the impact of additional adhesive treatment with glass-ionomer cement (GIC) was evaluated. METHODS: 250 intact molars were collected and randomly distributed into ten groups (n = 25). After endodontic procedure standard Class I cavities were prepared and restored with different direct restorative techniques and dentin-replacing materials. Two-group were restored with either packable or flowable short fiber-reinforced composites (SFRCs). Two-group were restored by experimental fiber-reinforced GIC with and without adhesive treatment. Four-group were restored by conventional and resin-modified GICs with or without adhesive treatment. One-group was restored with a dual-cure composite resin and last group was restored with only conventional composite resin (control). Fatigue-survival was measured for all specimens using a cyclic-loading machine until fracture occurred or a number of 40.000 cycles were achieved. Kaplan-Meyer survival analysis was conducted, followed by pairwise log-rank post hoc comparisons. Fracture mode was then examined by means of optical microscopy and SEM. RESULTS: Group restored with flowable SFRC showed significantly higher survival (p < 0.05) compared to all of the groups, except for group restored with packable SFRC (p > 0.05). Group restored with fiber-reinforced GIC had significantly (p < 0.05) higher survival rates compared to other commercial GICs. SEM demonstrated change of the fracture line when fracture reached the SFRC layer. SIGNIFICANCE: Direct restoration of Class I in ET molars with the use of SFRCs as dentin-replacing materials demonstrated its ability to reinforce the dental structures and to increase the fatigue resistance in this specific clinical situation.

Fatigue performance of endodontically treated premolars restored with direct and indirect cuspal coverage restorations utilizing fiber-reinforced cores.

OBJECTIVES: The aim of this in vitro study was to investigate the fatigue survival and fracture behavior of endodontically treated (ET) premolars restored with different types of post-core and cuspal coverage restorations. MATERIALS AND METHODS: MOD cavities were prepared on 108 extracted maxillary premolars. During the endodontic treatment, all teeth were instrumented with rotary files (ProTaper Universal) to the same apical enlargement (F2) and were obturated with a matched single cone obturation. After the endodontic procedure, the cavities were restored with different post-core and overlay restorations (n = 12/group). Three groups (A1-A3) were restored with either conventional composite core (PFC; control) or flowable short-fiber-reinforced composite (SFRC) core with/without custom-made fiber posts and without overlays. Six groups had similar post-core foundations as described above but with either direct PFC (B1-B3) or indirect CAD/CAM (C1-C3) overlays. Fatigue survival was tested for all restorations using a cyclic loading machine until fracture occurred or 50,000 cycles were completed. Kaplan-Meyer survival analysis was conducted, followed by pairwise post hoc comparisons. RESULTS: None of the restored teeth survived all 50,000. Application of flowable SFRC as luting-core material with fiber post and CAD/CAD overlays (Group C3) showed superior performance regarding fatigue survival (p < 0.05) to all the other groups. Flowable SFRC with fiber post and direct overlay (Group B3) showed superior survival compared to all other direct techniques (p < 0.05), except for the same post-core foundation but without cuspal coverage (Group A3). CONCLUSIONS: Custom-made fiber post and SFRC as post luting core material with or without cuspal coverage performed well in terms of fatigue resistance and survival when used for the restoration of ET premolars. CLINICAL RELEVANCE: The fatigue survival of direct and indirect cuspal coverage restorations in ET MOD premolars is highly dependent on whether the core build-up is fiber-reinforced or not. The combination of short and long fibers in the form of individualized post-cores seems to offer a favorable solution in this situation.