Biocompatibility of mineral trioxide aggregate flow and biodentine.

AIM: To evaluate the influence of powder-to-gel ratio (0.19 g powder to 50 µL of gel, thick MTA Flow, and 0.06 g powder to 50 µL of gel, fluid MTA Flow) on biocompatibility of MTA Flow (Ultradent Products Inc., South Jordan, UT, USA, lot: 2015122901) and compare it with Biodentine (Septodont Inc., Saint-Maur-des-Fossés, France, lot: B18542A). METHODOLOGY: The materials were manipulated and inserted into polyethylene tubes for implantation in twenty rats. After 7, 15, 30 and 60 days, the specimens were removed and embedded in paraffin. Haematoxylin and eosin sections were used to count the number of inflammatory cells (IC) and fibroblasts mm-2 (Fb). In the Masson's trichrome-stained sections, the fibrous capsule thickness was measured; picrosirius red-stained sections were used for birefringent collagen quantification. The data were submitted to two-way ANOVA and Tukey test (P ≤ 0.05). RESULTS: A significantly lower number of IC and consequently higher number of Fb were observed in the capsules adjacent to thick MTA Flow at all periods, in comparison with other materials (P ≤ 0.05). At 60 days, the quantity of birefringent collagen was significantly greater in the tissue in contact with thick MTA Flow, when compared with fluid MTA Flow and Biodentine. CONCLUSIONS: Although thick MTA Flow induced a less intense inflammatory response, all evaluated materials are biocompatible because they allowed regression of this process after 60 days.

Odontología minimamente invasiva para el tratamiento del desgaste dental / Minimally invasive dentistry for the treatment of tooth wear

El desgaste dental patológico, ocasionado por el bruxismo, es una alteración que se observa frecuentemente en la clínica odontológica. En este caso clínico fue realizado un procedimiento mínimamente invasivo, a fin de restablecer una guía anterior alterada por desgaste dental, asociado a otros tratamientos, tales como, el blanqueamiento dental y el ajuste oclusal. Este abordaje restaurador directo, asociado a las otras técnicas, posibilitó la máxima preservación de estructura dental remanente, alcanzando un excelente resultado estético y funcional, con una correcta adaptación del sistema estomatognático. (AU)

The dental tooth wear due to bruxism is an alteration that is seen frequently in the today ́s clinic. In this clinical case, a mini-mal invasive procedure was conducted aiming to restore the altered anterior guide by bruxism, associating other treatments, such as occlusal adjustment and bleaching. This direct restorative approach associated to the aforementioned treatments, made possible the maximum preservation of the tooth structure, reaching excellent functional and esthetic results, with a correct adaptation of the stomatognathic system. (AU)

Enamel wetness effects on bond strength using different adhesive systems.

OBJECTIVE: To evaluate, through the application of different dentin bonding systems, the influence of wetness on shear bond strength in enamel. METHODS: This study evaluated three etch-and-rinse adhesive systems (Scotchbond MP [used with and without primer]; Singlebond; and Prime&Bond 2.1) and two self-etching adhesive systems (Clearfil SE Bond; and Xeno IV). Flat bovine enamel surfaces were either air-dried for 30 seconds or blotted with absorbent paper after acid-etching for the conventional bonding agents or before the application of self-etching bonding agents. The resin composite EsthetX was bonded to flat surfaces that had been treated with one of the adhesives, following the manufacturer's instructions. After being stored in water at 37°C for one week, bonded specimens were broken in shear. Data were evaluated with two-way analysis of variance (ANOVA) and Student-Newman-Keuls tests (α=0.05). For comparing each condition individually, regardless of the adhesive or wetness condition, a one-way ANOVA and a Student-Newman-Keuls test (α=0.05) were applied. RESULTS: The two-way ANOVA showed significant differences among adhesive systems. An interaction effect was also observed (p<0.05), but wetness did not influence shear bond strength (p=0.98). The one-way ANOVA showed that the all-in-one adhesive was the only material influenced by the presence of water at the enamel's surface. CONCLUSION: The all-in-one adhesive behaved differently depending on whether the enamel surface was dry or wet.

Integrated orthodontic and restorative procedures for replacement of lost central incisors.

UNLABELLED: The use of adhesive material in association with many clinical procedures has contributed a great deal to solving functional and esthetic problems. Before adhesive techniques were known, dental procedures were more invasive and aggressive, especially in young patients. This article describes some integrated clinical procedures used to esthetically and functionally restore a mouth with traumatic loss of both central incisors. The treatment involved the orthodontic mesialization of the upper teeth toward the midline followed by anatomic and functional recovery through restorative dentistry. CLINICAL SIGNIFICANCE: This article describes some integrated clinical procedures that may effectively and conservatively improve the esthetic and functional results when a young patient loses the central incisors.

Fracture strength of weakened human premolars restored with amalgam with and without cusp coverage.

PURPOSE: To determine the effect of cusp coverage with amalgam restorations on the fracture strength of weakened human maxillary premolars. MATERIALS AND METHODS: 30 extracted human maxillary premolars were divided into three groups; Group A (control): uncut teeth, Group B: wide MOD cavities prepared and the pulp chamber's roof removed. The teeth were restored with amalgam without cusp coverage, Group C: same as Group B plus cusp reduction and restored with amalgam. The teeth were included in metal rings with self-curing polystyrene resin and stored in water for 24 hrs. The restorations were refined with rubber points, polished and further stored in water for 24 hrs before being subjected to a compressive axial load in a Universal testing machine at 0.5 mm/min. RESULTS: The mean fracture strength obtained was: Group A: 173.3 Kgf, Group B: 47.3 Kgf and Group C: 127.7 Kgf. All values were statistically significantly different (P < 0.05). The amalgam restoration of weakened human premolars with cusp coverage amalgam significantly increased the fracture strength of the teeth (63%) as compared to teeth restored without cusp coverage. The results showed that cusp coverage with amalgam might be an option for restoring weakened endodontically-treated teeth.

Tensile strength of five types of retention for resin-bonded prostheses.

The tensile bond strengths of five retention techniques for bonded cast restorations were tested. The retentive methods were the electrolytic etch, Rochette's perforations, retention beads, the recessed surface, and soldered orthodontic mesh. The electrolytic etch and recessed surface methods gave the highest values of bond strength, followed by retention beads. Rochette's perforations and the soldered orthodontic mesh failed to surpass the bond strength of the control group (no additional retention) after 1 hour and provided the lowest bond strength after 24 hours.

Metallurgical evaluation of a copper-based alloy for dental castings.

The present study was designed to evaluate the metallurgical properties of an experimental, low-cost copper-zinc-aluminum-nickel alloy for dental castings. Some specimens were subjected to heat treatment after induction casting. The extent of corrosion was determined by measuring weight loss of specimens stored in a sodium sulfite solution. In the as-cast specimens, tests demonstrated the presence of three phases: the first consisted of copper-zinc-aluminum, the second was similar but lower in copper and aluminum, and the third consisted of an intermetallic compound of manganese-nickel-phosphorus. After heat treatment, the first phase remained relatively constant, the second was converted to Cu3Al, and the third increased in volume. The weight loss from the as-cast specimens was eight times that of the heat-treated specimens. It was concluded that the heat treatment substantially changed the microstructure and improved the corrosion resistance of the experimental alloy.

[Effect of heat treatment on the structure of a Cu-Zn-Al-Ni system dental alloy]. / Efeito do tratamento térmico na estrutura da liga odontológica do sistema Cu-Zn-Al-Ni.

This article characterizes the structural phases present in the copper-based metallic alloy system "Cu-Zn-Al-Ni" developed for dental use, and relates those phases to other properties. The characterization was obtained after casting (using the lost wax process), and after heat treatment. In order to obtain better corrosion resistance by changing the microstructure, the castings were submitted to 30, 45 and 60 minutes of heat treatment at the following temperatures: 750 degrees C, 800 degrees C, and 850 degrees C. The various phases were analyzed using X-ray diffraction and scanning electron microscopy (SEM). The results after heat treatment showed a phase (probably Cu3Al), that could be responsible for the improvement in the alloy's resistance to corrosion as compared to the as-cast structure.

[Determination of casting contraction of alternative copper based alloys]. / Determinação da contração de fundição de ligas alternativas à base de cobre.

This study is about the cast contraction of 10 alternative alloys developed in the Dentistics Department of the Faculdade de Odontologia de Bauru that were compared with type III and type IV gold alloys and alternative commercial alloys.