Pullulan is an important polysaccharide with several potential applications in food science, pharmaceutical and cosmetic industries, but high costs of pullulan production are the main limitation for commercial utilization. Therefore, a cost-effective process for pullulan production was developed using fig syrup as an exclusive nutrient source. In particular, the feasibility of using low quality fig syrup as a supplemental substrate for pullulan gum production by Aureobasidium pullulans was investigated. Fermentation was carried out over a range of fig syrup and sucrose degrees Brix (5-15%). Maximum pullulan gum production was observed after 96h using 12.5% fig syrup, yielding approximately14.06 g/L. This value of pullulan production (14.06 g/L) was higher than the amount of pullulan produced using sucrose as substrate (5.01 g/L). In conclusion, fig syrup was an effective substrate for pullulan production by Aureobasidium pullulans, and, therefore, this byproduct deserves attention for the cost-effective and environmentally friendly pullulan production.

Alyssum homolocarpum seed gum-polyvinyl alcohol biodegradable composite film: Physicochemical, mechanical, thermal and barrier properties.

Films made from Alyssum homolocarpum seeds gum (AHSG) have poor mechanical and barrier (to oxygen) properties. In the present study poly vinyl alcohol (PVA) was used to improve the physicochemical properties of AHSG films. Results indicated that the addition of PVA significantly increased the moisture content, solubility, elongation at break (EB) and transparency while it decreased the density, oxygen permeability, chroma, water contact angle and Young modulus of AHSG based films. Films with higher AHSG to PVA ratios had lower water vapor permeability (WVP). The light barrier measurements presented low values of transparency at 600nm for PVA/AHSG films, indicating that films were very transparent while they had excellent barrier properties against UV light. Results for FTIR, DSC and SEM showed a clear interaction between PVA and AHSG, forming a new material. These results indicated that PVA/AHSG blend films had good compatibility.