RESUMO
STATEMENT OF THE PROBLEM: Candida species are believed to play an important role in initiation and progression of denture stomatitis. The type of the denture material also influences the adhesion of candida and development of stomatitis. PURPOSE: The aim of this study was comparing the adherence of candida albicans to the conventional and injection molding acrylic denture base materials. MATERIALS AND METHOD: Twenty injection molding and 20 conventional pressure pack acrylic discs (10×10×2 mm) were prepared according to their manufacturer's instructions. Immediately before the study, samples were placed in sterile water for 3 days to remove residual monomers. The samples were then sterilized using an ultraviolet light unit for 10 minutes. 1×108 Cfu/ml suspension of candida albicans ATCC-10231 was prepared from 48 h cultured organism on sabouraud dextrose agar plates incubated at 37oC. 100 µL of this suspension was placed on the surface of each disk. After being incubated at 37oC for 1 hour, the samples were washed with normal saline to remove non-adherent cells. Attached cells were counted using the colony count method after shaking at 3000 rmp for 20 seconds. Finally, each group was tested for 108 times and the data were statistically analyzed by t-test. RESULTS: Quantitative analysis revealed that differences in colony count average of candida albicans adherence to conventional acrylic materials (8.3×103) comparing to injection molding acrylic resins (6×103) were statistically significant (p<0.001). CONCLUSION: Significant reduction of candida albicans adherence to the injection acrylic resin materials makes them valuable for patients with high risk of denture stomatitis.
RESUMO
Sodium ascorbate has recently been suggested to compensate decreased bond strength of composite resin to bleached tooth surfaces. The aim of present study was to evaluate the effect of 10% sodium ascorbate on bleached bovine enamel morphology and microhardness considering the possibility of its effect on enamel surface characteristics. A total of 69 bovine enamel slabs were prepared and mounted in acrylic resin. Subsequent to polishing, they were randomly divided into 3 groups of 23 specimens each; 3 for Scanning Electron Microscopy (SEM) analysis and 20 for hardness test. In group 1 the specimens were immersed in distilled water as control group; in group 2 the specimens were bleached with 35% carbamide peroxide for 30 min a week for 3 consecutive weeks; and in group 3 the specimens were exposed to 10% sodium ascorbate for 30 min subsequent to bleaching similar to group 1. After 3 weeks Vickers hardness of the specimens was measured at 3 points with equal distances from each other under a force of 50 g. The mean of the hardness values of each specimen was calculated and data was analyzed by one-way ANOVA (P < 0.05). The highest and lowest microhardness values were observed in group 1 and group 2, respectively. However, there were no statistically significant differences in microhardness between the groups (P = 0.12). The use of 35% carbamide peroxide alone or with 10% sodium ascorbate does not affect bovine enamel hardness. SEM analysis showed a network of sodium ascorbate adsorbed to the bleached enamel surface.