Kinetics of Austenite Phase Transformations in Newly-Developed 0.17C-2Mn-1Si-0.2Mo Forging Steel with Ti and V Microadditions.

This work presents the results of phase transformation kinetics during continuous cooling in newly developed high strength low-alloy steel (HSLA). Initial theoretical calculations for the determination of heat treatment parameters were conducted. To determine the structural constituents formed due to the austenite decomposition the dilatometry approach was used. The material was cooled down from the austenitization temperature of 1000 °C with cooling rates between 0.1 °C/s to 60 °C/s. Then, light and scanning electron microscopy investigations were carried out. The microstructure after cooling at rates between 0.1 °C/s up to 1 °C/s is mainly ferritic with some fraction of granular bainite. Increasing the cooling rate led to formation of a higher fraction of bainitic ferrite. At 60 °C/s the microstructure was mainly bainite with some fraction of ferrite. To determine the presence of retained austenite, color etching using Klemm solution was used. The results show that the increase of cooling rate decreases the amount of retained austenite in the microstructure of the steel. Hardness measurements were made to determine the changes in the mechanical properties as a function of the cooling rate.

Dilatometric Analysis of the Austenite Decomposition in Undeformed and Deformed Low-Carbon Structural Steel.

This paper aims to analyze the effect of deformation on the phase transformation kinetics of low-carbon structural steel. The steel used for the investigation was subjected to two different dilatometric analyses using a DIL 805A/D device. The first analysis was to determine the phase transformation kinetics without deformation of austenite before cooling. Then, the analysis under deformation conditions was conducted to investigate the deformation effect on the transformation kinetics. Microscopic studies by light microscopy were performed. The essential part of the research was hardness analysis for different cooling rates and the creation of continuous-cooling-transformation (CCT) and deformation continuous-cooling-transformation (DCCT) diagrams. It was found that the deformation of the samples before cooling increases a diffusion rate in the austenite resulting in the corresponding increase of ferritic, pearlitic, and bainitic start temperatures, as well as shifting the austenite transformation product regions to a longer time. The increase of the transformation area and a decrease in grain size are observed for the deformed samples.

Dilatometric and Microstructural Study of Martensite Tempering in 4% Mn Steel.

This paper presents the results of martensite tempering resistance in 4% Mn steel. The material was quenched and tempered at 350 °C for 15, 30, and 60 min. The analysis of the quenching and tempering was carried out using dilatometric and microstructural approaches. The phase composition was assessed using X-ray diffraction. The Ms temperature and tempering progress were simulated using JMatPro software. The dilatometric analysis revealed a small decrease in the relative change in length (RCL) during tempering. This decrease was connected to the precipitation kinetics of cementite within the martensite laths. The microstructure investigation using a scanning electron microscope showed a very small amount of carbides, even for the longest tempering time. This showed the high tempering resistance of the martensite in medium-Mn steels. The hardness results showed an insignificant decrease in the hardness depending on the tempering time, which confirmed the high tempering resistance of martensite.

Dilatometric Study of Phase Transformations in 5 Mn Steel Subjected to Different Heat Treatments.

The work presents results of phase transformation kinetics of hot-rolled 5% Mn steel subjected to different heat treatments. Three different schedules were introduced: isothermal holding in a bainite region, coiling simulation and intercritical annealing. The evolution of microstructure components was investigated using dilatometric and metallographic analyses. According to obtained results, the medium-Mn steel exhibits high resistance for γ/α transformation during the bainite transformation and coiling simulation (upon cooling from the austenite region). During 5 h isothermal holding, no bainite and/or ferrite formation was detected. This results in the formation of martensite upon cooling to room temperature. Differently, when the steel was subjected to the intercritical annealing at 720 and 700 °C (upon heating from room temperature), a final microstructure consisted of ferrite, martensite and retained austenite. At 700 °C, no fresh martensite formation was detected upon cooling to room temperature. This means that the austenite was enriched in carbon during the intercritical annealing step enough to keep its thermal stability.

Effect of Hot Deformation on Phase Transformation Kinetics in Isothermally Annealed 3Mn-1.6Al Steel.

The kinetics of ferritic transformation and the corresponding microstructural evolution in 0.17C-3.1Mn-1.6Al-0.04Nb-0.22Mo-0.22Si medium-Mn steel during isothermal annealing was investigated in dilatometric studies. The material was subjected to thermal and thermo-mechanical treatments aimed at obtaining, by the austenite → ferrite transformation, a sufficient fraction of ferrite to stabilize the retained austenite by C and eventual Mn partitioning. The samples were isothermally held for 5 h in a temperature range from 600 to 750 °C to simulate simplified temperature conditions of an industrial coiling process following hot rolling. Some of the samples were plastically deformed at a temperature of 900 °C before isothermal holding in order to study the effect of hot deformation on the kinetics of phase transformations. After the dilatometric investigations the material was subjected to light and scanning electron microscopy to reveal relationships between the holding temperature, deformation and microstructure evolution. Hardness tests were performed to assess the mechanical behavior. A significant effect of manganese in slowing down diffusional transformations during the cooling of steel was found. The influence of austenite deformation on the kinetics of austenite to ferrite transformation was noted. The plastically deformed samples showed an accelerated start of ferritic transformation and the extension of its range. During dilatometric tests, low-range dynamic ferritic transformation was recorded, which was also confirmed by the microscopic tests.

Explanation of the PLC Effect in Advanced High-Strength Medium-Mn Steels. A Review.

The paper reviews the recent works concerning the Portevin-Le Chatelier (PLC) effect in Advanced High-Strength Steels (AHSSs) with a special attention to high-strength medium-manganese steels. Theories explaining the mechanism of the plastic instability phenomenon in steels with medium- and high-Mn contents were discussed. The relationships between microstructural effects such as TRIP (Transformation-Induced Plasticity), TWIP (Twinning-Induced Plasticity) and the PLC effect were characterized. The effects of processing conditions including a deformation state (hot-rolled and cold-rolled) and strain parameters (deformation temperature, strain rate) were addressed. Factors affecting the value of critical strain for the activation of serrated flow behavior in particular in medium-manganese steels were described.