In Vitro Effects of Resin Infiltration on Enamel Erosion Inhibition.

Resin-based materials that show promising effects for preventing the progression of erosion have been studied. This in vitro study evaluated the effects of applying resin-based materials, including resin infiltration, on previously eroded enamel subjected to erosive challenges. The influence of enamel surface etching prior to application of the material was also studied. Bovine enamel blocks were immersed in hydrochloric acid (HCl), 0.01 M (pH 2.3), for 30 seconds in order to form a softened erosion lesion. The blocks were then randomly divided into nine groups (n=12) and treated as follows: C = control without treatment; Hel = pit & fissure resin sealant (Helioseal Clear); Adh = two-step self-etching adhesive system (AdheSe); Tet = two-step conventional adhesive system (Tetric N-bond); and Inf = infiltrant (Icon). The Helno, Adhno, Tetno, and Infno groups received the same materials without (or with no) surface conditioning. The depth of the material's penetration into softened erosion lesions was qualitatively analyzed using reflection and fluorescence confocal microscopy. After application of the materials, the blocks were immersed in HCl for two minutes; this step was followed by immersion in artificial saliva for 120 minutes four times a day for five days (erosive cycling). Both the enamel alteration and material thickness were analyzed using profilometry, and the results were submitted to Kruskal-Wallis and Dunn tests (p>0.05). Images from the confocal microscopy showed minimal penetration of Adh/Adhno and deep penetration of Inf/Infno into the erosive lesions. The groups Hel, Adh, Inf, Tetno, and Infno resulted in the formation of a layer of material over the enamel, which was effective in inhibiting the progression of erosion. In conclusion, the infiltrant, with or without etching, was able to penetrate and protect the enamel against dental erosion. The other resin-based materials, except for the two-step conventional adhesive, were able to penetrate and inhibit the progression of erosive lesions only when they were applied after enamel etching.

Effect of fluoride varnish supplemented with sodium trimetaphosphate on enamel erosion and abrasion: an in situ/ex vivo study.

OBJECTIVE: To evaluate the effect of fluoride (F) varnishes supplemented or not with sodium trimetaphosphate (TMP) on enamel erosive wear followed or not by abrasion in situ. METHODS: Ten volunteers were selected and randomly divided into four groups, according to the varnishes tested: placebo (no F or TMP), 5% NaF (positive control), 2.5% NaF and 2.5% NaF/5% TMP. Enamel blocks (n=4) were mounted in palatal devices and received an application of each test varnish, following a double-blind, crossover protocol. After 6h, varnishes were completely removed and the blocks were subjected to erosive challenges by ex vivo immersion in citric acid (5 min, 4×/dia, 5 days). Following, half of the blocks were subjected to abrasion by brushing with a placebo dentifrice slurry for 15s. Enamel wear (µm), surface hardness (SHf) and cross-sectional hardness (ΔKHN) were assessed after each experimental period. Results were analyzed by ANOVA, Student-Newman-Keuls's test and Pearson correlation coefficient (p<0.05). RESULTS: The fluoride varnish supplemented with TMP promoted significantly lower wear and ΔKHN when compared to the other groups after erosive challenges, followed or not by abrasion (p<0.05). As for (SHf) the fluoride varnish supplemented with TMP promoted similar results to the 5% NaF product, being significantly higher than the remaining groups after erosive and erosive+abrasive challenges (p<0.05). CONCLUSION: TMP significantly enhanced the effects of F on enamel wear after erosive challenges, followed or not by abrasion.

Effect of different fluoride concentrations of experimental dentifrices on enamel erosion and abrasion.

It has been suggested that fluoride products are able to reduce erosive tooth wear. Thus, the purpose of this in vitro study was to evaluate the effect of dentifrices with different fluoride concentrations as well as of a low-fluoridated dentifrice supplemented with trimetaphosphate (TMP) on enamel erosion and abrasion. One hundred twenty bovine enamel blocks were assigned to the following experimental dentifrices: placebo, 1,100 microg F/g, 500 microg F/g plus 3% TMP and 5,000 microg F/g. The groups of enamel blocks were additionally subdivided into conditions of erosion (ERO) and of erosion plus abrasion (ERO + ABR). For 7 days, the blocks were subjected to erosive challenges (immersion in Sprite 4 times a day for 5 min each time) followed by a remineralizing period (immersion in artificial saliva between erosive challenges for 2 h). After each erosive challenge, the blocks were exposed to slurries of the dentifrices (10 ml/sample for 15 s). Sixty of the blocks were additionally abraded by brushing using an electric toothbrush (15 s). The alterations of the enamel were quantified using the Knoop hardness test and profilometry (measurements in micrometers). The data were analyzed using a 2-way ANOVA test followed by a Bonferroni correction (p < 0.05). In in vitro conditions, the 5,000 microg F/g and 500 microg F/g plus 3% TMP dentifrices had a greater protective effect when compared with the 1,100 microg F/g dentifrice, under both ERO and ERO + ABR conditions. The results suggest that dentifrices alone are not capable of completely inhibiting tooth wear.