Experimental Simulation of Directional Crystallization of SiMo Cast Iron Alloyed with Al and Cr.

SiMo ductile cast iron combines ease of part fabrication with good mechanical properties, including a usable plasticity range. Its poor corrosion resistance inherited from grey cast iron could be alleviated through alloying with Al or Cr additions capable of forming a dense oxide scale protecting the substrate. However, the presence of Al and Cr in cast iron tends to make the material brittle, and their optimum alloying additions need to be studied further. The present work was aimed at investigating the effect of crystallization rates on microstructure changes during directional crystallization of SiMo-type alloys with up to 3.5% Al and 2.4% Cr. The experiment was performed using the Bridgman-Stockbarger method. The tubular crucible was transferred from the hot section to cold section at rates ranging from 5 mm/h to 30 mm/h with a 4/5 crucible length and then quenched. The introduced Al promoted graphitization up to a point, wherein, at the highest applied addition, the graphite precipitation preceded crystallization of the rest of the melt. A rising level of Cr in these alloys from 1% to 2.4% resulted in the formation of low and high contents of pearlite, respectively. The higher crystallization rates proved effective in increasing the ferrite content at the expense of pearlite. In the investigated cast iron samples with smaller applied alloying additions, Widmanstätten ferrite or ausferrite, i.e., fine acircular phase, were often found. The switch from directional crystallization to quenching caused a transition from a liquid to solid state, which started with nucleation of islands of fine austenite dendrites with chunky graphite eutectic separating them. As these islands expanded, they pushed alloying additions to their sides, promoting carbide or pearlite formation in these places and forming a super-cell-like structure. The performed experiments helped gather information concerning the sensitivity of the microstructure of SiMo cast iron modified with Al and Cr to crystallization rates prevailing in heavy cast structures.

Evaluation of Microstructure and Abrasive Wear-Resistance of Medium Alloy SiMo Ductile Cast Iron.

Medium-alloy ductile iron with a SiMo ferritic matrix has very good heat resistance. The addition of chromium and aluminum also increases this resistance. This article presents the impact of chromium and aluminum on the structure of SiMo cast iron, especially their impact on the deformation of the spherical graphite precipitates and the formation of M6C and M3C2 carbide phases. These carbides are formed in a ferritic matrix or at the grain boundaries, resulting in increased hardness and a drastic reduction in impact strength. The article presents the influence of heat treatment on the material's microstructure and resistance to abrasive wear. Chromium and aluminum additions can also indirectly reduce the abrasive wear resistance of SiMo cast iron. The presented research shows the possibility of doubling the abrasive wear resistance of SiMo cast iron.