Influence of different curing modes on flexural properties, fracture toughness, and wear behavior of dual-cure provisional resin-based composites.

We investigated the influence of different curing modes on the mechanical properties and wear behavior of dual-cure provisional resin-based composites (DCPRs). Three DCPRs and a self-curing bis-acryl provisional resin-based composite were used. Flexural strength (σF), elastic modulus (E), resilience (R), and fracture toughness (KIC) were measured. The specimens were fabricated with and without light irradiation, stored in distilled water at 37°C for 24 h, and subjected to 5,000 or 10,000 thermal cycles. For sliding impact wear testing, 12 specimens were prepared with and without light irradiation. The maximum facet depth and volume loss were determined using a noncontact profilometer. Some of the mechanical properties and wear behavior of DCPRs are affected by light irradiation. This study indicated that proper light irradiation is important in polymerization process of the DCPRs to enhance the wear resistance and some mechanical properties.

Effect of a coating material containing surface reaction-type pre-reacted glass-ionomer filler on prevention of primary enamel demineralization detected by optical coherence tomography.

We used optical coherence tomography to examine the effect of a coating material containing surface reaction-type pre-reacted glass-ionomer (S-PRG) filler on primary enamel demineralization in 18 extracted human primary teeth. The pulp was removed, and each tooth was ultrasonically cleaned with distilled water. Six teeth were treated with 0.1-M lactic acid buffer solution (De group). In the second group (n = 6), a thin film of coating material was applied before demineralization (PRG group). A third group (Control group; n = 6) was maintained in artificial saliva. Using optical coherence tomography, we measured peak signal intensity (dB) and width at 1/e2 (µm) at predetermined locations on the enamel surface and calculated integrated values. All data were analyzed with ANOVA and the Tukey-Kramer test (α = 0.05). Although changes in integrated values differed between groups, there was a small but significant increase in the Control group and a small but significant decrease in the De group. In the PRG group, integrated values were significantly higher at 7 days after the start of the experiment and significantly increased thereafter. Our findings indicate that a coating material containing S-PRG fillers may prevent primary enamel demineralization.

Effect of light irradiation and primer application on polymerization of selfadhesive resin cements monitored by ultrasonic velocity.

In this study, we investigated the effect of light irradiation and primer/adhesive application on the polymerization reaction and elastic modulus (E) of self-adhesive resin cement (SAC) through ultrasonic velocity (V) measurements. The V values of longitudinal and shear waves were determined based on the transit time through the specimens and specimen thicknesses, and were used to calculate the E values. Analysis of variance and Tukey tests revealed that V increased rapidly, reaching a plateau at 2,700-2,900 m/s, when the SACs were light-irradiated. However, the increasing rate of V was retarded for the non-irradiated SACs. In addition, when the primer/adhesive was applied, higher E values were obtained after 24 h. Finally, the polymerization behavior of the SACs was affected by light irradiation and primer application, and the use of prime/adhesive might improve mechanical properties. In clinical situations, use of primer/adhesive is recommended for getting proper adhesion.