Enhanced retention of polymer physical characteristics and mechanical strength of 70:30 poly(L-lactide-co-D,L-lactide) after ethylene oxide sterilization.

This study examined the effect of ethylene oxide (EtO) and electron beam (e-beam) irradiation on the properties of 70:30 poly(L-lactide-co-D,L-lactide). The effects of sterilization upon the polymer physical characteristics and strength retention of the material were examined, both initially and after being subjected to real time ageing. Commercially available 70:30 poly(L-lactide-co-D,L-lactide) material was fabricated into rectangular, cylindrical, screw, and sheet designs, and tested in compression, shear, or tension. Sterilization of 70:30 poly(L-lactide-co-D,L-lactide) by ethylene oxide had a nearly negligible effect on the physical properties of the polymer, regardless of specimen size or manufacturing technique. The molecular weight and inherent viscosity of the specimens decreased by approximately 3% after sterilization by EtO. However, sterilization of 70:30 poly(L-lactide-co-D,L-lactide) by e-beam irradiation resulted in immediate changes to some of the physical properties of the polymer. Specimens sterilized by e-beam irradiation displayed an immediate decrease in inherent viscosity of approximately 67% as compared to the respective nonsterile samples. The immediate decrease in inherent viscosity and molecular weight with e-beam irradiation required approximately 39 weeks of real time ageing of the EtO sterilized parts. At all time points investigated in the present study, the strength retention of the EtO sterilized devices equaled or exceeded that of the e-beam irradiated samples.

Characterization of a faster resorbing polymer after real time aging.

This study evaluated the in vitro strength retention and polymer characteristics of specimens made from commercially available 85:15 poly(D,L-lactide-co-glycolide). Test samples included dogbone tensile specimens with a nominal thickness of either 0.75 and 1.0 mm, which were machined from compression-molded sheets, and screws with a major diameter of 2.71 mm and minor diameter of 2.14 mm, which were manufactured by injection molding. All samples were sterilized by e-beam irradiation prior to in vitro aging following a standard methodology. Mechanical testing and polymer analysis were performed at time zero and weekly up to 15 weeks of real time aging. The time zero maximum tensile strength of the 0.75 mm dogbone specimens averaged 55.86 +/- 0.72 MPa. The 1.0-mm dogbone specimens tested at time zero had an average maximum tensile strength of 34.55 +/- 0.36 MPa. The 0.75-mm and 1.0-mm thick dogbone specimens exhibited a controlled decrease in their tensile strength. The initial shear strength of the injection-molded screws was 32.86 +/- 4.15 MPa. After 3 weeks of real time in vitro aging, the screws maintained approximately 70% of their initial (time zero) strength. The inherent viscosity and molecular weight (Mw) at time zero averaged approximately 0.9 dL/g and 98,000 g/mol respectively, and decreased at similar rates for both dogbones and screws. These results demonstrate a controlled, rapid degradation in the mechanical properties of 85:15 poly(D,L-lactide-co-glycolide) material, with sufficient strength for pediatric craniofacial applications.

Strength retention of 70:30 poly(L-lactide-co-D,L-lactide) following real-time aging.

This study evaluated the in vitro strength retention and polymer characteristics of plates and screws made from commercially available 70:30 poly(L-lactide-co-D,L-lactide) over a 2-year time period. Test samples included three routine manufacturing lots each of plates (1.2 mm thick, 41.70 mm long, with 2.5-mm holes), which were machined from compression-molded sheets, and screws (2.4-mm major diameter and 1.86-mm minor diameter), which were manufactured by injection molding. All samples were sterilized by e-beam irradiation prior to in vitro aging following a standard methodology. Mechanical testing and polymer analysis was performed after 0, 6, 13, 26, 39, 52, 65, 78, and 104 weeks. The initial (time zero) tensile strength of the plates averaged 33.2+/-1.9 MPa; the plates retained 100% of this strength at 6 weeks, 84% at 13 weeks, and 34% at 39 weeks. The screws had an initial (time zero) shear strength of 29.8+/-4.2 MPa, and maintained 97% of this strength at 26 weeks and 73% of this strength at 39 weeks. The inherent viscosity and molecular weight (M(w)) at time zero averaged approximately 1.4 dL/g and 165,000 g/mol, respectively, and decreased at similar rates for both the plates and screws. These results demonstrate excellent strength retention of devices fabricated from 70:30 poly(L-lactide-co-D,L-lactide) over time periods exceeding those associated with normal bone healing.