Retention of Manually or CAD/CAM-customized Fiberglass Posts Luted to Enlarged Root Canals with Different Resin Cements.

The aim of this laboratory study was to evaluate the pull-out force of a prefabricated fiberglass post (PP), relined fiberglass post (RP), or milled fiberglass post (MP) luted with Multilink N (MN), RelyX Unicem 2 (RXU2) or RelyX Ultimate (RU) to enlarged root canals. The thickness of the resin cements and the presence of voids in the resin cement film were observed. The root canals of 90 bovine incisors were enlarged, endodontically treated, and randomly divided into 9 groups (n=10) according to the post type and resin cement. The specimens were scanned using micro-CT to analyze the thickness of the resin cement and the presence of voids. The specimens were submitted to mechanical cyclic loading (500,000 cycles at 50 N load) and subjected to pull-out force testing. Two-way ANOVA and Tukey's test analyzed the pull-out force and resin cement thickness data. Kruskal-Wallis and Bonferroni tests analyzed the void scores. The interaction between factors (post × resin cement) was significant (p=0.0001) for the pull-out force. Higher pull-out forces were obtained for RP and MP compared to PP. The post factor was significant (p=0.0001) for resin cement thickness, which was higher for PP (1054 µm), followed by MP (301 µm) and RP (194 µm). More void formation occurred for PP, being less for RP, differing significantly among the posts. Post customization (RP and MP) decreased resin cement thickness and void formation, favoring a higher pull-out force. Resin cements requiring an adhesive application (MN and RU) favored higher pull-out force than self-adhesive resin cement (RXU2).

CAD/CAM Milled Glass Fiber Posts: Adaptation and Mechanical Behavior in Flared Root Canals.

This study aimed to evaluate the cementation and mechanical behavior of flared root canals restored with CAD/CAM milled glass fiber post-and-core systems. Sixty-six endodontically treated human canines with a flared root canal were divided into three different groups according to the type of post: GPF received prefabricated posts; GREL received relined glass fiber posts, and GMILLED received CAD/CAM milled glass fiber posts. Cementation was performed with self-adhesive resin cement. The samples were submitted to x-ray microcomputed tomography analysis for the analysis of voids and gaps. The roots were sectioned and submitted to the push-out bond strength test. The load-to-fracture was evaluated in post-and-core systems. GMILLED presented lower void and lower gap volumes when compared to GPF and GREL. On the load-to-fracture test, GREL presented statistically significant higher values than GMILLED. GPF values had no statistically significant difference from the two other groups. On the push-out bond strength test, GPF presented statistically significant lower values when compared to GREL and GMILLED. The most common failure pattern was between dentin and cement in all groups. CAD/CAM milled glass fiber post-and-core systems presented an enhanced adaptation of glass fiber posts to flared root canal systems. Their results were comparable to relined posts in bond strength, while load-to-fracture-results for GMILLED were lower than those for GPF.

Computational modelling of the antischistosomal activity for neolignan derivatives based on the MIA-SAR approach.

Theoretical models for exploring the antischistosomal activity of a dataset of 18 synthetic neolignans are built using the multivariate image analysis applied to structure-activity relationships (MIA-SAR) approach. The obtained models were validated using the accuracy (Acc) in leave-one-out cross-validation, external validation and Y-randomization procedures, yielding correct classification superior to 80%, 70% and 60%, respectively. Additionally, a comparison was made of the models obtained from binary (black and white) and coloured images; the colours (pixel values) were selected to correspond to chemical properties. It was observed that the models obtained from coloured images with pixel values corresponding to electronegativity (known as the aug-MIA-SAR(colour) approach) generally yielded superior statistical parameters compared with those obtained from binary images (MIA-SAR) and randomly coloured images (atoms are coloured according to their type) with atomic sizes corresponding to Van der Waals radius (aug-MIA-SAR), respectively. Mechanistic interpretation of the influence of different substituents on the antischistosomal activity revealed that methoxy substituents in the R1 (or R2) and R5 positions of the neolignan scaffold are indispensable for the antischistosomal activity. The obtained results provide knowledge of the possible structural modifications to yield novel neolignan compounds with antischistosomal activity.

Influence of immediate dentin sealing techniques on cuspal deflection and fracture resistance of teeth restored with composite resin inlays.

SUMMARY This research evaluated the influence of immediate dentin sealing (IDS) techniques on cuspal deflection and fracture resistance of teeth restored with composite resin inlays. Forty-eight maxillary premolars were divided into four groups: G1, sound teeth (control); G2, without IDS; G3, IDS with Clearfil SE Bond (CSE); and G4, IDS with CSE and Protect Liner F. The teeth from groups 2, 3, and 4 received mesio-distal-occlusal preparations. The impressions were made with vinyl polysiloxane, followed by provisional restoration and storage in water for seven days. The impressions were poured using type IV die stone, and inlays with Filtek Z250 composite resin were built over each cast. The inlays were luted with Panavia F. After storage in water for 72 hours, a 200-N load was applied on the occlusal surface using a metal sphere connected to a universal testing machine, and the cuspal deflection was measured with a micrometer. The specimens were then submitted to an axial load until failure. The following mean cuspal deflection (µm) and mean fracture resistance (N) followed by the same lowercase letter represent no statistical difference by analysis of variance and Tukey (p<0.05): cuspal deflection: G1, 3.1 ± 1.5(a); G2, 10.3 ± 4.6(b); G3, 5.5 ± 1.8(ac); and G4, 7.7 ± 5.1(bc); fracture resistance: G1, 1974 ± 708(a); G2, 1162 ± 474(b); G3, 700 ± 280(b); and G4, 810 ± 343(b). IDS with CSE allowed cuspal deflection comparable with that associated with sound teeth. The application of Protect Liner F did not contribute to a decrease in cuspal deflection. The IDS techniques did not influence the fracture resistance of teeth.

Effect of two microwave disinfection protocols on adaptation of poly (methyl methacrylate) denture bases.

AIM: A few protocols of microwave irradiation have been proposed for disinfection of dental prostheses, but their effect on dimensional alteration still is unknown. This study evaluated the effect of 2 protocols of microwave disinfection on adaptation of resin denture bases polymerised by conventional hot water bath or by microwave energy. METHODS: Thirty-six resin bases were obtained from stone casts duplicated from a metallic master model of an edentulous maxilla and polymerised by either conventional hot water bath or microwave energy. Experimental disinfection treatments were: 1) control (no disinfection); 2) protocol 1 (690 W/6 min); 3) protocol 2 (345 W/6 min). Disinfection procedures were performed 3 times (T1, T2, T3) with a 7-day interval. Adaptation was measured by weighing a vinyl polysiloxane film reproducing the gap between resin base and master model. Data were analysed by ANOVA for repeated measures and Bonferroni test (a=0.05). RESULTS: In T1 and T2, all groups polymerised by microwave energy had higher mean values than the groups polymerised by conventional technique. In T3, denture resin bases polymerised by microwave energy had increased poor adaptation when submitted to microwave disinfection at 690 W for 6 min. No significant changes were found for bases submitted to microwave disinfection at 345 W for 6 min (P>0.05). CONCLUSIONS: Adaptation of denture bases varied as a function of polymerisation technique and protocol of microwave disinfection (power and time) over time. Microwave disinfection at 690 W for 6 min proved harmful to denture bases after repeated disinfection procedures.