1.
Chem Mater ; 36(3): 1579-1590, 2024 Feb 13.
Artigo em Inglês | MEDLINE | ID: mdl-38370283

RESUMO

Several synthetic methods have recently emerged to develop high-surface-area solid-state organic framework-based materials into free-flowing liquids with permanent porosity. The fluidity of these porous liquid (PL) materials provides them with advantages in certain storage and transport processes. However, most framework-based materials necessitate the use of cryogenic temperatures to store weakly bound gases such as H2, temperatures where PLs lose their fluidity. Covalent organic framework (COF)-based PLs that could reversibly form stable complexes with H2 near ambient temperatures would represent a promising development for gas storage and transport applications. We report here the development, characterization, and evaluation of a material with these remarkable characteristics based on Cu(I)-loaded COF colloids. Our synthetic strategy required tailoring conditions for growing robust coatings of poly(dimethylsiloxane)-methacrylate (PDMS-MA) around COF colloids using atom transfer radical polymerization (ATRP). We demonstrate exquisite control over the coating thickness on the colloidal COF, quantified by transmission electron microscopy and dynamic light scattering. The coated COF material was then suspended in a liquid polymer matrix to make a PL. CO2 isotherms confirmed that the coating preserved the general porosity of the COF in the free-flowing liquid, while CO sorption measurements using diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) confirmed the preservation of Cu(I) coordination sites. We then evaluated the gas sorption phenomenon in the Cu(I)-COF-based PLs using DRIFTS and temperature-programmed desorption measurements. In addition to confirming that H2 transport is possible at or near mild refrigeration temperatures with these materials, our observations indicate that H2 diffusion is significantly influenced by the glass-transition temperature of both the coating and the liquid matrix. The latter result underscores an additional potential advantage of PLs in tailoring gas diffusion and storage temperatures through the coating composition.

2.
J Phys Chem C Nanomater Interfaces ; 126(35): 14801-14812, 2022 Sep 08.
Artigo em Inglês | MEDLINE | ID: mdl-36110496

RESUMO

Materials that are capable of adsorbing and desorbing gases near ambient conditions are highly sought after for many applications in gas storage and separations. While the physisorption of typical gases to high surface area covalent organic frameworks (COFs) occurs through relatively weak intermolecular forces, the tunability of framework materials makes them promising candidates for tailoring gas sorption enthalpies. The incorporation of open Cu(I) sites into framework materials is a proven strategy to increase gas uptake closer to ambient conditions for gases that are capable of π-back-bonding with Cu. Here, we report the synthesis of a Cu(I)-loaded COF with subnanometer pores and a three-dimensional network morphology, namely Cu(I)-COF-301. This study focused on the sorption mechanisms of hydrogen, ethylene, and carbon monoxide with this material under ultrahigh vacuum using temperature-programmed desorption and Kissinger analyses of variable ramp rate measurements. All three gases desorb near or above room temperature under these conditions, with activation energies of desorption (E des) calculated as approximately 29, 57, and 68 kJ/mol, for hydrogen, ethylene, and carbon monoxide, respectively. Despite these strong Cu(I)-gas interactions, this work demonstrated the ability to desorb each gas on-demand below its normal desorption temperature upon irradiation with ultraviolet (UV) light. While thermal imaging experiments indicate that bulk photothermal heating of the COF accounts for some of the photodriven desorption, density functional theory calculations reveal that binding enthalpies are systematically lowered in the COF-hydrogen matrix excited state initiated by UV irradiation, further contributing to gas desorption. This work represents a step toward the development of more practical ambient temperature storage and efficient regeneration of sorbents for applications with hydrogen and π-accepting gases through the use of external photostimuli.

3.
ACS Appl Mater Interfaces ; 11(28): 25115-25122, 2019 Jul 17.
Artigo em Inglês | MEDLINE | ID: mdl-31264402

RESUMO

Catalytic MoSx thin films have been directly photoelectrodeposited on GaInP2 photocathodes for stable photoelectrochemical hydrogen generation. Specifically, the MoSx deposition conditions were controlled to obtain 8-10 nm films directly on p-GaInP2 substrates without ancillary protective layers. The films were nominally composed of MoS2, with additional MoOxSy and MoO3 species detected and showed no long-range crystalline order. The as-deposited material showed excellent catalytic activity toward the hydrogen evolution reaction relative to bare p-GaInP2. Notably, no appreciable photocurrent reduction was incurred by the addition of the photoelectrodeposited MoSx catalyst to the GaInP2 photocathode under light-limited operating conditions, highlighting the advantageous optical properties of the film. The MoSx catalyst also imparted enhanced durability toward photoelectrochemical hydrogen evolution in acidic conditions, maintaining nearly 85% of the initial photocurrent after 50 h of electrolysis. In total, this work demonstrates a simple method for producing dual-function catalyst/protective layers directly on high-performance, planar III-V photoelectrodes for photoelectrochemical energy conversion.