This paper presents an approach for hydrolyzing cellulose nanocrystals from oil palm empty fruit bunch (OPEFB) presented through hydrochloric acid hydrolysis under sonication-hydrothermal conditions. Differences in concentration, reaction time, and acid-to-cellulose ratio affect toward the yield, crystallinity, microstructure, and thermal stability were obtained. The highest yield of cellulose nanocrystals up to 74.82%, crystallinity up to 78.59%, and a maximum degradation temperature (Tmax) of 339.82 °C were achieved through hydrolysis using 3 M HCl at 110 °C during 1 h. X-ray diffraction analysis indicated a higher diffraction peak pattern at 2θ = 22.6° and a low diffraction peak pattern at 2θ = 18°. All cellulose nanocrystals showed a crystalline size of under 1 nm, and it was indicated that the sonication-hydrothermal process could reduce the crystalline size of cellulose. Infrared spectroscopy analysis showed that a deletion of lignin and hemicellulose was demonstrated in the spectrum. Cellulose nanocrystal morphology showed a more compact structure and well-ordered surface arrangement than cellulose. Cellulose nanocrystals also had good thermal stability, as a high maximum degradation temperature was indicated, where CNC-D1 began degrading at temperatures (T0) of 307.09 °C and decomposed (Tmax) at 340.56 °C.