In this study, the synthesis of a MXene (Ti3C2Tx)-derived TiO2/starbon (M-TiO2/Starbon-800 °C) nanocomposite using a facile calcination method is explored. High-temperature exposure transforms layered Ti3C2Tx into rod-like TiO2 and starbon into amorphous carbon. The resulting M-TiO2/Starbon-800 °C nanocomposite exhibits a significantly larger surface area and pore volume compared to its individual components, leading to superior electrochemical performance. In a three-electrode configuration, the nanocomposite achieved a specific capacitance (Csp) of 1352 Fg⻹ at 1 Ag⻹, while retaining more than 99% of its Csp after 50 000 charge/discharge cycles. Furthermore, when incorporated into a two-electrode symmetric coin cell, it demonstrates a Csp of 115 Fg⻹ along with exceptional long cycle life. Moreover, the device shows an energy density (ED) of 51 Whkg-1 and a power density (PD) of 7912 Wkg-1 at 5 Ag-1. The enhanced charge storage is attributed to the formation of a porous structure with a high specific surface area resulting from the interaction between M-TiO2 nanorods and starbon, which facilitates efficient ion penetration.