RESUMO
Roughening of Ti6Al4V by blasting with alumina or zirconia particles improves the mechanical fixation of implants by increasing the surface area available for bone/implant apposition. Additional thermal oxidation treatments of the blasted alloy have already shown to be a complementary low-cost solution to enhancing the in vitro biocompatibility and corrosion resistance of the alloy. In this work, the effects of oxidation treatment on a grit blasted Ti6Al4V biomedical alloy have been analysed in order to understand the net effect of the combined treatments on the alloy fatigue properties. Synchrotron radiation diffraction experiments have been performed to measure residual stresses before and after the treatments and microstructural and hardness changes have been determined. Although blasting of Ti6Al4V with small spherical zirconia particles increases the alloy fatigue resistance with respect to unblasted specimens, fatigue strength after oxidation decreases below the unblasted value, irrespective of the type of particle used for blasting. Moreover, at 700°C the as-blasted compressive residual stresses (700MPa) are not only fully relaxed but even moderate tensile residual stresses, of about 120MPa, are found beneath the blasted surfaces. Contrary to expectations, a moderate increase in hardness occurs towards the blasted surface after oxidation treatments. This can be attributed to the fact that grit blasting modifies the crystallographic texture of the Ti6Al4V shifting it to a random texture, which affects the hardness values as shown by additional experiments on cold rolled samples. The results indicate that the oxidation treatment performed to improve biocompatibility and corrosion resistance of grit blasted Ti6Al4V should be carried out with caution since the alloy fatigue strength can be critically diminished below the value required for high load-bearing components.
Assuntos
Cerâmica/química , Estresse Mecânico , Temperatura , Titânio/química , Ligas , Dureza , Teste de Materiais , Oxirredução , Propriedades de SuperfícieRESUMO
Calculations of the induced currents created in the human body by external electromagnetic fields would be more accurate provided that more realistic experimental values of the electrical properties of the body were available. The purpose of this work is to experimentally obtain values for the conductivity of living organs in conditions close to the real situation. Two-electrode in vivo measurements of the bioimpedance of some porcine organs have been performed. From these measurements and taking into account geometrical considerations, the electrical conductivity for the kidney, liver, heart, and spinal cord has been obtained and were found to be higher than the values reported in the literature. Furthermore, a new experimental procedure is proposed where the conductivity is determined from the values of the electrical potential and currents that are induced by an external electromagnetic field created by a coil placed close to the organ under study.
Assuntos
Condutividade Elétrica , Suínos , Animais , Eletrodos , Campos Eletromagnéticos , Humanos , Especificidade de ÓrgãosRESUMO
This study reports on the biocompatibility of 316 LVM steel blasted with small and rounded ZrO(2) particles or larger and angular shaped Al(2)O(3) particles. The effect of blasting on the in vitro corrosion behavior and the associated ion release is also considered. Surface of Al(2)O(3) blasted samples was rougher than that of ZrO(2) blasted samples, which was also manifested by a higher surface area. Compared to the polished alloy, blasted steels exhibited a lower corrosion resistance at the earlier stages of immersion, particularly when using Al(2)O(3) particles. With increasing immersion time, blasted samples experienced an improvement of the corrosion resistance, achieving impedance values typical of passive alloys. Blasting of the alloy led to an increase in Fe release and the leaching of Ni, Mn, Cr and Mo. On all surfaces, ion release is higher during the first 24 h exposure and tends to decrease during the subsequent exposure time. Despite the lower corrosion resistance and higher amount of ions released, blasted alloys exhibit a good biocompatibility, as demonstrated by culturing osteoblastic cells that attached and grew on the surfaces.
Assuntos
Materiais Biocompatíveis , Aço Inoxidável , Corrosão , Propriedades de SuperfícieRESUMO
Patterned surfaces direct cell spatial dynamics, yielding cells oriented along the surface geometry, in a process known as contact guidance. The Rho family of GTPases controls the assembly of focal adhesions and cytoskeleton dynamics, but its role in modulating bone-cell alignment on patterned surfaces remains unknown. This article describes the interactions of two human cell types involved in osseointegration, specifically mesenchymal stem cells and osteoblasts, with submicron- or nano-scale Ti6Al4V grooved surfaces generated by mechanical abrasion. The surface chemistry of the alloy was not affected by grinding, ensuring that the differences found in cellular responses were exclusively due to changes in topography. Patterned surfaces supported cell growth and stimulated mesenchymal stem cell viability. Anisotropic surfaces promoted cell orientation and elongation along the grates. Both cell types oriented on nanometric surfaces with grooves of 150 nm depth and 2 µm width. The number of aligned cells increased by approximately 30% on submicrometric grooves with sizes of about 1 µm depth and 10 µm width. Cells were treated with drugs that attenuate the activities of the GTPase RhoA and one of its downstream effectors, Rho-associated kinase (ROCK), and contact guidance of treated cells on the grooved surfaces was investigated. The data indicate that the RhoA/ROCK pathway is a key modulator of both mesenchymal stem cell and osteoblast orientation on nanometric surface features. RhoA and its effector participate in the alignment of mesenchymal stem cells on submicrometric grooves, but not of osteoblasts. These findings show that RhoA/ROCK signaling is involved in contact guidance of bone-related cells on metallic substrates, although to a varying extent depending on the specific cell type and the dimensions of the pattern.
Assuntos
Comunicação Celular/efeitos dos fármacos , Células-Tronco Mesenquimais/citologia , Osteoblastos/citologia , Transdução de Sinais/efeitos dos fármacos , Titânio/farmacologia , Quinases Associadas a rho/metabolismo , Proteína rhoA de Ligação ao GTP/metabolismo , 1-(5-Isoquinolinasulfonil)-2-Metilpiperazina/análogos & derivados , 1-(5-Isoquinolinasulfonil)-2-Metilpiperazina/farmacologia , ADP Ribose Transferases/farmacologia , Ligas , Anisotropia , Toxinas Botulínicas/farmacologia , Sobrevivência Celular/efeitos dos fármacos , Citoesqueleto/efeitos dos fármacos , Citoesqueleto/metabolismo , Humanos , Células-Tronco Mesenquimais/efeitos dos fármacos , Osteoblastos/efeitos dos fármacos , Propriedades de Superfície/efeitos dos fármacosRESUMO
The purpose of this work is to study the changes of the bioimpedance from its 'in vivo' value to the values measured in a few hours after the excision from the body. The evolution of electrical impedance with time after surgical extraction has been studied on two porcine organs: the liver and the kidney. Both in vivo and ex vivo measurements of electrical impedance, measuring its real and imaginary components, have been performed. The in vivo measurements have been carried out with the animal anaesthetized. The ex vivo measurements have been made more than 2 h after the extraction of the organ. The latter experiment has been carried out at two different stabilized temperatures: at normal body temperature and at the standard preservation temperature for transplant surgery. The measurements show a correlation between the biological evolution and the electrical bioimpedance of the organs, which increases from its in vivo value immediately after excision, multiplying its value by 2 in a few hours.
Assuntos
Rim/fisiologia , Fígado/fisiologia , Suínos , Animais , Temperatura Corporal , Impedância Elétrica , Eletrodos , Fatores de TempoRESUMO
In this Letter, we report on a crucial experiment showing that magnetic impurities reduce the ferromagnetic order temperature in thiol-capped Au glyconanoparticles (GNPs). The spontaneous magnetization of AuFe GNPs exhibits a fast decrease with temperature that contrasts with the almost constant value of the magnetization observed in Au NPs. Moreover, hysteresis disappears below 300 K. Both features indicate that Fe impurities reduce the high local anisotropy field responsible for the ferromagnetic behavior in Au GNPs. As a consequence, the amazing ferromagnetism in Au NPs should not be associated with the presence of magnetic impurities.
RESUMO
PM2000 is a ferritic alloy obtained by powder metallurgy and is being investigated for potential applications as a biomaterial. This work aimed to assess the biological compatibility and to determine the influence of the processing route and further recrystallisation treatment on the magnetic behaviour. The magnetic behaviour has been analysed as a function of the hysteresis loop obtained by using an inductive method. The biocompatibility has been tested using human osteoblast-like cells seeded onto discs of PM2000. The ability of cells, on its surface, to attach, grow, and produce alkaline phosphatase (ALP) was determined. It is shown that PM2000 is a soft magnetic material irrespective of its material condition, its remanent magnetisation being very low (up to about 3% for the recrystallised swaged material). Fields close to 200 Oe are required to saturate the material. The saturation magnetisation is about 135 emu g(-1). In vitro tests indicate that cells are able to attach and grow onto its surface, and produce ALP, a specific marker of cells with bone-forming activity. In this respect, PM2000 holds promise as a suitable substrate for bone integration. These properties could make PM2000 a useful candidate for the preparation of medical devices where biocompatible and soft magnetic materials are sought. Applications for dental magnetic attachments could be envisaged.
Assuntos
Alumínio/química , Materiais Biocompatíveis/química , Cromo/química , Cristalização/métodos , Ferro/química , Magnetismo , Osteoblastos/citologia , Osteoblastos/fisiologia , Titânio/química , Adesão Celular/fisiologia , Linhagem Celular , Proliferação de Células , Sobrevivência Celular/fisiologia , Humanos , Teste de Materiais , Microesferas , Osseointegração/fisiologia , Tamanho da Partícula , Propriedades de SuperfícieRESUMO
We report on the experimental observation of magnetic hysteresis up to room temperature in thiol-capped Au nanoparticles with 1.4 nm size. The coercive field ranges from 860 Oe at 5 K to 250 Oe at 300 K. It is estimated that the Au atoms exhibit a magnetic moment of mu=0.036mu(B). However, Au nanoparticles with similar size but stabilized by means of a surfactant, i.e., weak interaction between protective molecules and Au surface atoms, are diamagnetic, as bulk Au samples are. The apparent ferromagnetism is consequently associated with 5d localized holes generated through Au-S bonds. These holes give rise to localized magnetic moments that are frozen in due to the combination of the high spin-orbit coupling (1.5 eV) of gold and the symmetry reduction associated with two types of bonding: Au-Au and Au-S.