Fate of plastic film residues in agro-ecosystem and its effects on aggregate-associated soil carbon and nitrogen stocks.

Biodegradable (Bio) plastic films are widely viewed as promising alternative products of low-density polyethylene (LDPE) films to minimize plastic debris accumulation and pollution in agroecosystems. Yet, this speculation indeed lacks of sufficient evidences. We conducted a landfill investigation on the aging characteristics of Bio and LDPE plastic films in maize field, and the effects on soil aggregate composition and carbon & nitrogen stocks. The degradation rate of Bio film was up to 41.1% while that of LDPE film was zero. Scanning electron microscope (SEM) showed that the crack formation of Bio film had a pronounced domino effect, and FTIR showed that old Bio film displayed an extra wide peak threshold ranging from 3000 to 3500 cm-1. Particularly, the abundance of microplastics was elevated with the increased plastic residues, and the increment mostly resulted from Bio residues. Critically, plastic residues significantly lowered the soil macro-aggregates (>0.25 mm) proportion, while increasing that of micro-aggregates (0.1-0.25 mm) in LDPE, and silt/clay fraction (<0.1 mm) in Bio respectively. They significantly promoted total nitrogen content of the aggregates with the same size, but decreased the organic carbon content, dramatically lowering the C/N. Therefore, we first identified the fate of plastic film residues in agroecosystems and revealed the serious deficiencies of Bio plastic film.

Effects of increased plastic film residues on soil properties and crop productivity in agro-ecosystem.

Intensive use of low-density polyethylene (LDPE) plastic films in agro-ecosystems has raised considerable concerns due to the increasing film residues in soils. It is unclear how the increased film residues affect soil properties and crop productivity and whether biodegradable (Bio) film can substitute LDPE. To address the issue, we designed a landfill experiment with different addition levels of plastic residue into soils of maize (Zea mays L.) field from 2018 to 2019. Six treatments were arranged as PMT1-T3/BioT1-T3, representing the low, medium, and high-level application of LDPE / Bio film fragments, with no residual film, applied as CK. Results show that, soil bulk density was significantly increased from 1.19 to 1.31 g/cm3 regardless of residue types. In contrast, soil porosity was lowered from 58.03% in CK to 57.36% in Bio and 56.12% in LDPE significantly (P < 0.05). Increased residues improved soil nitrogen level and lowered the C/N ratio significantly. Also, it decreased microbial biomass C and N levels but with no change in C/N (P < 0.05). Maize yield and WUE decreased, while soil water storage increased significantly. LDPE residues affected soil properties and productivity partly lower than Bio ones did, but the negative effects of them were similar in the maize field.