Determination of the Oxygen Content in the LiF-NaF-KF Melt.

The present paper is dedicated to the quantitative determination of oxygen-containing impurities in the LiF-NaF-KF eutectic using electrochemical (cyclic and square-wave voltammetry) and reduction melting methods. The LiF-NaF-KF melt was analyzed before and after purifying electrolysis. The amount of oxygen-containing impurities removed from the salt during purification was determined. It was found that after electrolysis, the concentration of oxygen-containing impurities decreased by 7 times. The results obtained via electrochemical techniques and reduction melting were well-correlated, which made it possible to evaluate the quality of the LiF-NaF-KF F melt. To verify the analysis conditions, mechanical mixtures of LiF-NaF-KF containing Li2O were analyzed using the reduction melting method. The oxygen concentration in the mixtures varied from 0.672 to 2.554 wt. %. Based on the analysis results, the dependence approximated by the straight line was obtained. These data may be used to draw calibration curves and to further develop the procedure of oxygen analysis of fluoride melts.

Thermal Conductivity of FLiNaK in a Molten State.

Although the thermal conductivity of molten salt mixtures is of interest for many potential technological applications, precise values are often hard to obtain. In this study, the thermal diffusivity of FliNaK was studied in a molten state using the laser flash method and found to be very slightly dependent on temperature. The heat capacity of FliNaK was measured using the DSC method. There was a minor difference between our results and data from the literature. From calculations based on thermal diffusivity, density and heat capacity values, thermal conductivity was shown to decrease with temperature.

Corrosion Behavior of Candidate Functional Materials for Molten Salts Reactors in LiF-NaF-KF Containing Actinide Fluoride Imitators.

Molten fluorides of alkali metals are considered a technological medium for molten salt reactors (MSRs). However, these media are known to be extremely corrosive. The successful implementation of high-temperature technological devices using molten alkali metal fluorides requires the selection of such structural materials that have high corrosion resistance in melts with compositional characteristic of MSRs. In this research, the corrosion behavior of 12Cr18Ni10Ti steel, the alloy Ni60Cr20Mo15, and the alloy Monel 404 (Ni50Cu50) was investigated in the LiF-NaF-KF eutectic melt, containing additions of CeF3 and NdF3 from 0 to 5 wt.% as imitator fluorides of actinides in an inert argon atmosphere at 550 °C for 100 h. Gravimetry, energy-dispersive X-ray (EDX) microanalysis of surfaces and cross-section of samples, and ICP-MS were used to establish the corrosion behavior of the investigated alloys. Corrosion resistance of the studied materials was found to decrease in a row from Monel 404 > Hastelloy C2000 > 12Cr18Ni10Ti. The addition of cerium fluoride into the melt resulted in the additional etching of the alloy surface. The addition of neodymium fluoride resulted in the formation of the point/inter-crystalline corrosion damages in the sample bulk. The samples of steel 12Cr18Ni10Ti were subjected to local cracking corrosion. The austenitic nickel-based alloys suffered specific local corrosion with formation of subsurface voids. Excellent corrosion resistance of the Monel alloy under the test conditions was found.

Investigation of the Quasi-Binary Phase Diagram FLiNaK-NdF3.

The NdF3 solubility in molten eutectic FLiNaK, which is a conceivable medium for a molten salt reactor (MSR), was determined by the quasi-binary phase diagram FLiNaK-NdF3. The eutectic mixture FLiNaK was prepared by direct melting of components LiF, NaF and KF·HF. The acidic anhydrous salt (KF·HF) was used instead of the hygroscopic KF. The NdF3 was sintered by hydrofluorination of Nd2O3. The oxygen impurity in the prepared eutectic FLiNaK, determined by an oxygen analyzer LECO OH836, was 0.036 wt.%, whereas the NdF3 contained 0.04 wt.% of oxygen. A part of the FLiNaK-NdF3 quasi-binary phase diagram was obtained using two thermal analysis techniques: differential thermal analysis (DTA) and differential scanning calorimetry (DSC). The FLiNaK-NdF3 phase diagram in the region of 0-30 mol.% NdF3 contains one eutectic at 2 mol.% NdF3 and 450 °C and two peritectic points: 8 mol.% NdF3 at 500 °C and 22 mol.% NdF3 at 575 °C. The region of the FLiNaK-NdF3 phase diagram below the liquidus line is rather complicated due to the complex structure of the multicomponent system in its molten state, as in its solid state. The NdF3 solubility in FLiNaK is about 5 mol.% at 490 °C and 29 mol.% at 700 °C; this means that the process of the MA transmutation in the MSR can be carried out in molten FLiNaK with a content of actinides as high as 15-20 mol.% in the temperature range of 550-650 °C.