New micro/mesoporous nanocomposite material from low-cost sources for the efficient removal of aromatic and pathogenic pollutants from water.

A new micro/mesoporous hybrid clay nanocomposite prepared from kaolinite clay, Carica papaya seeds, and ZnCl2 via calcination in an inert atmosphere is presented. Regardless of the synthesis temperature, the specific surface area of the nanocomposite material is between ≈150 and 300 m2/g. The material contains both micro- and mesopores in roughly equal amounts. X-ray diffraction, infrared spectroscopy, and solid-state nuclear magnetic resonance spectroscopy suggest the formation of several new bonds in the materials upon reaction of the precursors, thus confirming the formation of a new hybrid material. Thermogravimetric analysis/differential thermal analysis and elemental analysis confirm the presence of carbonaceous matter. The new composite is stable up to 900 °C and is an efficient adsorbent for the removal of a water micropollutant, 4-nitrophenol, and a pathogen, E. coli, from an aqueous medium, suggesting applications in water remediation are feasible.

Microwave-Assisted Synthesis of Defects Metal-Imidazolate-Amide-Imidate Frameworks and Improved CO2 Capture.

In this work, we report three isostructural 3D frameworks, named IFP-11 (R = Cl), IFP-12 (R = Br), and IFP-13 (R = Et) (IFP = Imidazolate Framework Potsdam) based on a cobalt(II) center and the chelating linker 2-substituted imidazolate-4-amide-5-imidate. These chelating ligands were generated in situ by partial hydrolysis of 2-substituted 4,5-dicyanoimidazoles under microwave (MW)-assisted conditions in DMF. Structure determination of these IFPs was investigated by IR spectroscopy and a combination of powder X-ray diffraction (PXRD) with structure modeling. The structural models were initially built up from the single-crystal X-ray structure determination of IFP-5 (a cobalt center and 2-methylimidazolate-4-amide-5-imidate linker based framework) and were optimized by using density functional theory calculations. Substitution on position 2 of the linker (R = Cl, Br, and Et) in the isostructural IFP-11, -12, and -13 allowed variation of the potential pore window in 1D hexagonal channels (3.8 to 1.7 Å). The potential of the materials to undergo specific interactions with CO2 was measured by the isosteric heat of adsorption. Further, we resynthesized zinc based IFPs, namely IFP-1 (R = Me), IFP-2 (R = Cl), IFP-3 (R = Br), and IFP-4 (R = Et), and cobalt based IFP-5 under MW-assisted conditions with higher yield. The transition from a nucleation phase to the pure crystalline material of IFP-1 in MW-assisted synthesis depends on reaction time. IFP-1, -3, and -5, which are synthesized by MW-assisted conditions, showed an enhancement of N2 and CO2, compared to the analogous conventional electrical (CE) heating method based materials due to crystal defects.

Structural and analytical studies of silica accumulations in Equisetum hyemale.

Horsetail (Equisetum spp.) is known as one of the strongest accumulators of silicon among higher terrestrial plants. We use the combination of position-resolved analytical techniques, namely microtomography, energy-dispersive X-Ray elemental mapping, Raman microscopy, as well as small-angle and wide-angle scattering of X-rays, to study the type, distribution and nanostructure of silica in the internodes of Equisetum hyemale. The predominant silicification pattern is a thin continuous layer on the entire outer epidermis with the highest density in particular knob regions of the long epidermal cells. The knob tips contain up to 33 wt% silicon in the form of pure hydrated amorphous silica, while the silica content is lower in the inner part of the knobs and on the continuous layer. In contrast to the knob tips, the silica in these regions lacks silanol groups and is proposed to be in close association with polysaccharides. No mentionable amount of crystalline silica is detected by wide-angle X-ray scattering. The small-angle X-ray scattering data are consistent with the presence of colloidal, sheet-like silica agglomerates with a thickness of about 2 nm. From these results we conclude that there are at least two distinct forms of silica in E. hyemale which may have different functions. The close association of silica with cell wall polymers suggests that they may act as a polymeric template that controls the shape and size of the colloidal silica particles similar to many other biominerals and mineralised tissues. We propose that owing to its specific distribution in E. hyemale, a protective role and possibly also an important biomechanical role are among the most likely functions of silica in these plants.

Synthesis and characterization of SiC materials with hierarchical porosity obtained by replication techniques.

Porous silicon carbide monoliths were obtained using the infiltration of preformed SiO(2) frameworks with appropriate carbon precursors such as mesophase pitch. The initial SiO(2) monoliths possessed a hierarchical pore system, composed of an interpenetrating bicontinuous macropore structure and 13 nm mesopores confined in the macropore walls. After carbonization, further heat treatment at ca. 1,400 degrees C resulted in the formation of a SiC-SiO(2) composite, which was converted into a porous SiC monolith by post-treatment with ammonium fluoride solution. The resulting porous SiC featured high crystallinity, high chemical purity and showed a surface area of 280 m(2) g(-1) and a pore volume of 0.8 ml g(-1).