Gravity-driven hybrid membrane for oleophobic-superhydrophilic oil-water separation and water purification by graphene.

We prepared a simple, low-cost membrane suitable for gravity-driven oil-water separation and water purification. Composite membranes with selective wettability were fabricated from a mixture of aqueous poly(diallyldimethylammonium chloride) solution, sodium perfluorooctanoate, and silica nanoparticles. Simply dip-coating a stainless steel mesh using this mixture produced the oil-water separator. The contact angles (CAs) of hexadecane and water on the prepared composite membranes were 95 ± 2° and 0°, respectively, showing the oleophobicity and superhydrophilicity of the membrane. In addition, a graphene plug was stacked below the membrane to remove water-soluble organics by adsorption. As a result, this multifunctional device not only separates hexadecane from water, but also purifies water by the permeation of the separated water through the graphene plug. Here, methylene blue (MB) was removed as a demonstration. Membranes were characterized by high-resolution scanning electron microscopy (HRSEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared (FT-IR) spectroscopy to elucidate the origin of their selective wettability.

Carbon- and oxygen-free Cu(InGa)(SSe)2 solar cell with a 4.63% conversion efficiency by electrostatic spray deposition.

We have demonstrated the first example of carbon- and oxygen-free Cu(In,Ga)(SSe)2 (CIGSSe) absorber layers prepared by electrospraying a CuInGa (CIG) precursor followed by annealing, sulfurization, and selenization at elevated temperature. X-ray diffraction and scanning electron microscopy showed that the amorphous as-deposited (CIG) precursor film was converted into polycrystalline CIGSSe with a flat-grained morphology after post-treatment. The optimal post-treatment temperature was 300 °C for annealing and 500 °C for both sulfurization and selenization, with a ramp rate of 5 °C/min. The carbon impurities in the precursor film were removed by air annealing, and oxide that was formed during annealing was removed by sulfurization. The fabricated CIGSSe solar cell showed a conversion efficiency of 4.63% for a 0.44 cm(2) area, with Voc = 0.4 V, Jsc = 21 mA/cm(2), and FF = 0.53.