Low-temperature noninjection approach to homogeneously-alloyed PbSe(x)S(1-x) colloidal nanocrystals for photovoltaic applications.

Homogeneously alloyed PbSe(x)S(1-x) nanocrystals (NCs) with their excitonic absorption peaks in wavelength shorter than 1200 nm were developed for photovoltaic (PV) applications. Schottky-type solar cells fabricated with our PbSe0.3S0.7 NCs as their active materials reached a high power conversion efficiency (PCE) of 3.44%, with an open circuit voltage (V(oc)) of 0.49 V, short circuit photocurrent (J(sc)) of 13.09 mA/cm², and fill factor (FF) of 0.54 under Air Mass 1.5 global (AM 1.5G) irradiation of 100 mW/cm². The syntheses of the small-sized colloidal PbSe(x)S(1-x) NCs were carried out at low temperature (60 °C) with long growth periods (such as 45 min) via a one-pot noninjection-based approach in 1-octadecene (ODE), featuring high reaction yield, high product quality, and high synthetic reproducibility. This low-temperature approach employed Pb(oleate)2 as a Pb precursor and air-stable low-cost thioacetamide (TAA) as a S source instead of air-sensitive high-cost bis(trimethylsilyl)sulfide ((TMS)2S), with n-tributylphosphine selenide (TBPSe) as a Se precursor instead of n-trioctylphosphine selenide (TOPSe). The reactivity difference of TOPSe made from commercial TOP 90% and TBPSe made from commercial TBP 97% and TBP 99% was addressed with in situ observation of the temporal evolution of NC absorption and with ³¹P nuclear magnetic resonance (NMR). Furthermore, the addition of a strong reducing/nucleation agent diphenylphosphine (DPP) promoted the reactivity of the Pb precursor through the formation of a Pb-P complex, which is much more reactive than Pb(oleate)2. Thus, the reactivity of TBPSe was increased more than that of TAA. The larger the DPP-to-Pb feed molar ratio, the more the Pb-P complex, the higher the Se amount in the resulting homogeneously alloyed PbSe(x)S(1-x) NCs. Therefore, the use of DPP allowed reactivity match of the Se and S precursors and led to sizable nucleation at low temperature so that long growth periods became feasible. The present study brings insight into the formation mechanism of monomers, nucleation/growth of colloidal composition-tunable NCs, and materials design and synthesis for next-generation low-cost and high-efficiency solar cells.

Low-temperature approach to high-yield and reproducible syntheses of high-quality small-sized PbSe colloidal nanocrystals for photovoltaic applications.

Small-sized PbSe nanocrystals (NCs) were synthesized at low temperature such as 50-80 °C with high reaction yield (up to 100%), high quality, and high synthetic reproducibility, via a noninjection-based one-pot approach. These small-sized PbSe NCs with their first excitonic absorption in wavelength shorter than 1200 nm (corresponding to size < ∼3.7 nm) were developed for photovoltaic applications requiring a large quantity of materials. These colloidal PbSe NCs, also called quantum dots, are high-quality, in terms of narrow size distribution with a typical standard deviation of ∼7-9%, excellent optical properties with high quantum yield of ∼50-90% and small full width at half-maximum of ∼130-150 nm of their band-gap photoemission peaks, and high storage stability. Our synthetic design aimed at promotion of the formation of PbSe monomers for fast and sizable nucleation with the presence of a large number of nuclei at low temperature. For formation of the PbSe monomer, our low-temperature approach suggests the existence of two pathways of Pb-Se (route a) and Pb-P (route b) complexes. Either pathway may dominate, depending on the method used and its experimental conditions. Experimentally, a reducing/nucleation agent, diphenylphosphine, was added to enhance route b. The present study addresses two challenging issues in the NC community, the monomer formation mechanism and the reproducible syntheses of small-sized NCs with high yield and high quality and large-scale capability, bringing insight to the fundamental understanding of optimization of the NC yield and quality via control of the precursor complex reactivity and thus nucleation/growth. Such advances in colloidal science should, in turn, promote the development of next-generation low-cost and high-efficiency solar cells. Schottky-type solar cells using our PbSe NCs as the active material have achieved the highest power conversion efficiency of 2.82%, in comparison with the same type of solar cells using other PbSe NCs, under Air Mass 1.5 global (AM 1.5G) irradiation of 100 mW/cm(2).