Synthesis of mesoporous triple-metal nanosorbent from layered double hydroxide as an efficient new sorbent for removal of dye from water and wastewater.

In this study, co-precipitation synthesis of the mesoporous triple-metal nanosorbent from Fe, Cu, Ni layered double hydroxide (FeCuNi-LDH), on the basis of the data obtained from the TG analysis was carried out. The FTIR spectroscopy and XRD results confirm the formation of CuO, NiO and Fe2O3 nanoparticles, while the EDX analysis does not show significant variations on the surface in elemental composition. BET analysis shows that FeCuNi-280 (FeCuNi-LDH calcinated at 280 °C) with mesoporous structure, has larger surface area compared to FeCuNi-LDH and FeCuNi-550 (FeCuNi-LDH calcinated at 550 °C). The value of pHPZC of FeCuNi-280 is found to be 8.66. Obtained FeCuNi-280 material showed the ability for efficient removal of dye Reactive Blue 19 (RB19) from water, with a very high sorption capacity of 480.79 mg/g at optimal conditions: the sorbent dose of 0.6 g/dm3, stirring speed of 280 rpm and pH 2. The kinetics results of the sorption process were well fitted by pseudo-second order and Chrastil model, and the sorption isotherm was well described by Sips, Langmuir and Brouers-Sotolongo model. FeCuNi-280 was easily regenerated with aqueous solution of NaOH, and reutilization was successfully done in five sorption cycles. The present study show that easy-to-prepare, relatively inexpensive nanosorbent FeCuNi-280 is among the best sorbents for the removal of RB19 dye from water solution and wastewater from textile industry in wide range of pH.

A New Photocatalyst Bismuth Oxo Citrate: Synthesis, Characterization, and Photocatalytic Performance.

A new photocatalyst bismuth oxo citrate was synthesized by facile precipitation process with calcination at 200 °C. The photocatalyst was characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier-transform infrared (FTIR) spectroscopy, N2 sorptometry, and elemental analysis. Morphologically, it is composed of polyhedral particles with different, irregular shapes and sizes. The specific surface area (SSA) of the photocatalyst was 8.92 m2 g-1. It showed very good photocatalytic performance and reusability. Total decolorization of Reactive Blue 19 (RB19) was achieved in less than 10 minutes, which is much faster in comparison with TiO2 P25. Also, bismuth oxo citrate showed higher photocatalytic activity than other photocatalysts based on bismuth compounds reported by other authors. Optimal photocatalysis parameters were pH 2 and photocatalyst dose of 250 mg dm-3. The decolorization rate was found to decrease as initial dye concentration increased. The photocatalytic data best fitted to L-H kinetic model with pseudo-first order reaction rate. Chrastil diffusion model showed that diffusion has not influence on the process.