The origin of stability and high Co2+/3+ redox utilization for FePO4-coated LiCo0.90Ti0.05PO4/MWCNT nanocomposites for 5 V class lithium ion batteries.

Highly-dispersed 10 wt% FePO4 (FP)-coated LiCo0.90Ti0.05PO4 (LCTP) was successfully synthesized within a multiwalled carbon nanotube matrix via our original ultracentrifugation process. 10 wt% FP-coated LCTP sample showed a higher discharge capacity of 116 mA h g-1 together with stable cycle performance over 99% of capacity retention at the 100th cycle in high voltage. A combination of TEM, XRD, XPS, and XAFS analyses suggests that (i) Ti4+-substitution increases the utilization of Co redox (capacity increase) in LCP crystals by suppressing the Co3O4 formation and creating the vacancies in Co sites, and (ii) the FP-coating brought about the Fe enrichment of the surface of LCTP which prevents an irreversible crystal structure change and electrolyte decomposition during cycling, resulting in the stable cycle performance.

Enhanced Electrochemical Performance of Ultracentrifugation-Derived nc-Li3VO4/MWCNT Composites for Hybrid Supercapacitors.

Nanocrystalline Li3VO4 dispersed within multiwalled carbon nanotubes (MWCNTs) was prepared using an ultracentrifugation (uc) process and electrochemically characterized in Li-containing electrolyte. When charged and discharged down to 0.1 V vs Li, the material reached 330 mAh g(-1) (per composite) at an average voltage of about 1.0 V vs Li, with more than 50% capacity retention at a high current density of 20 A g(-1). This current corresponds to a nearly 500C rate (7.2 s) for a porous carbon electrode normally used in electric double-layer capacitor devices (1C = 40 mA g(-1) per activated carbon). The irreversible structure transformation during the first lithiation, assimilated as an activation process, was elucidated by careful investigation of in operando X-ray diffraction and X-ray absorption fine structure measurements. The activation process switches the reaction mechanism from a slow "two-phase" to a fast "solid-solution" in a limited voltage range (2.5-0.76 V vs Li), still keeping the capacity as high as 115 mAh g(-1) (per composite). The uc-Li3VO4 composite operated in this potential range after the activation process allows fast Li(+) intercalation/deintercalation with a small voltage hysteresis, leading to higher energy efficiency. It offers a promising alternative to replace high-rate Li4Ti5O12 electrodes in hybrid supercapacitor applications.

Ultrafast Nanocrystalline-TiO2 (B)/Carbon Nanotube Hyperdispersion Prepared via Combined Ultracentrifugation and Hydrothermal Treatments for Hybrid Supercapacitors.

Anisotropically grown (b-axis short) single-nano TiO2 (B), uniformly hyper-dispersed on the surface of multiwalled carbon nanotubes (MWCNT), was successfully synthesized via an in situ ultracentrifugation (UC) process coupled with a follow-up hydrothermal treatment. The uc-TiO2 (B)/MWCNT composite materials enable ultrafast Li(+) intercalation especially along the b-axis, resulting in a capacity of 235 mA h g(-1) per TiO2 (B) even at 300C (1C = 335 mA g(-1) ).

Progress of the conversion reaction of Mn3O4 particles as a function of the depth of discharge.

A comprehensive investigation of the morphological and interfacial changes of Mn3O4 particles at different lithiation stages was performed in order to improve our understanding of the mechanism of the irreversible conversion reaction of Mn3O4. The micronization of Mn3O4 into a Mn-Li2O nanocomposite microstructure and the formation of a solid electrolyte interphase (SEI) on the Mn3O4 surface were carefully observed and characterized by combining high-resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), and in situ X-ray absorption fine structure (XAFS) measurements. Accumulation of a thin SEI film of 2-5 nm thickness on the surfaces of the Mn3O4 particles due to their catalytic decomposition was observed at a depth of discharge (DOD) of 0%. As the DOD increases from 25% to 75%, the SEI layer composed of Li2CO3 and LiF continues to grow to 20-30 nm, and Li2O nanoparticles are clearly observed. At 100% DOD, the Mn-Li2O particles with diameters of 2-5 nm become totally encapsulated within a huge organic-inorganic coating structure, while the overall starting shape of the particles remains.

New generation "nanohybrid supercapacitor".

To meet growing demands for electric automotive and regenerative energy storage applications, researchers all over the world have sought to increase the energy density of electrochemical capacitors. Hybridizing battery-capacitor electrodes can overcome the energy density limitation of the conventional electrochemical capacitors because they employ both the system of a battery-like (redox) and a capacitor-like (double-layer) electrode, producing a larger working voltage and capacitance. However, to balance such asymmetric systems, the rates for the redox portion must be substantially increased to the levels of double-layer process, which presents a significant challenge. An in situ material processing technology called "ultracentrifuging (UC) treatment" has been used to prepare a novel ultrafast Li4Ti5O12 (LTO) nanocrystal electrode for capacitive energy storage. This Account describes an extremely high-performance supercapacitor that utilizes highly optimized "nano-nano-LTO/carbon composites" prepared via the UC treatment. The UC-treated LTO nanocrystals are grown as either nanosheets or nanoparticles, and both have hyperlinks to two types of nanocarbons: carbon nanofibers and supergrowth (single-walled) carbon nanotubes. The spinel structured LTO has been prepared with two types of hyperdispersed carbons. The UC treatment at 75 000G stoichiometrically accelerates the in situ sol-gel reaction (hydrolysis followed by polycondensation) and further forms, anchors, and grafts the nanoscale LTO precursors onto the carbon matrices. The mechanochemical sol-gel reaction is followed by a short heat-treatment process in vacuo. This immediate treatment with heat is very important for achieving optimal crystallization, inhibiting oxidative decomposition of carbon matrices, and suppressing agglomeration. Such nanocrystal composites can store and deliver energy at the highest rate attained to this date. The charge-discharge profiles indicate a very high sustained capacity of 80 mAh g(-1) at an extremely high rate of 1200 C. Using this ultrafast material, we assembled a hybrid device called a "nanohybrid capacitor" that consists of a Faradaic Li-intercalating LTO electrode and a non-Faradaic AC electrode employing an anion (typically BF4(-)) adsorption-desorption process. The "nanohybrid capacitor" cell has demonstrated remarkable energy, power, and cycleability performance as an electrochemical capacitor electrode. It also exhibits the same ion adsorption-desorption process rates as those of standard activated carbon electrodes in electrochemical capacitors. The new-generation "nanohybrid capacitor" technology produced more than triple the energy density of a conventional electrochemical capacitor. Moreover, the synthetic simplicity of the high-performance nanostructures makes it possible to scale them up for large-volume material production and further applications in many other electrochemical energy storage devices.