Synthesis and characterization of cobalt nanoparticles for application in the removal of textile dye.

In this work, magnetic cobalt nanoparticles (CoNPs) were synthesized and applied to the removal of Remazol golden yellow RNL (RGY) from aqueous solutions and textile wastewater. The CoNPs were characterized and the Co content found in the CoNPs was 60.38% (m/m). The analysis of X-ray Diffraction (XRD) and Raman Spectroscopy indicated the presence of Co0 and CoO in the composition of the material, as confirmed by Thermogravimetric Analysis coupled to Mass Spectrometry (TG-MS). Images obtained by the Transmission Electron Microscope (TEM) showed that the CoNPs have sizes smaller than 10 nm, sphere morphology and high agglomeration capacity. The results obtained by nitrogen adsorption-desorption suggested that the nanomaterial presented a mesoporous characteristic, low specific surface area (15.70 m2 g-1) and a pore volume and pore diameter of 0.072 cm3 g-1 and 3.64 nm, respectively. CoNPs removed the RGY with high efficiency, reaching almost 100% removal in 30 min. The kinetic results showed that the reaction followed pseudo-second-order kinetics. Additionally, the removal process can be altered depending on the experimental condition. For instance, under acidic conditions, the reductive degradation prevailed, while in neutral or basic conditions, two simultaneous processes occur: reductive degradation and adsorption. Finally, CoNPs were applied to textile wastewater. The results showed high discoloration, reaching almost 88%. However, there was only a 32% decrease in chemical oxygen demand, showing that CoNPs are efficient at removing organic dyes from aqueous solutions.

Sulfentrazone dechlorination by iron-nickel bimetallic nanoparticles.

The sulfentrazone dechlorination using bimetallic nanoparticles of Fe/Ni was studied. Different variables that could influence the sulfentrazone conversion were investigated, such as nitrogen atmosphere, pH and dosage of the nanoparticles and initial concentration of sulfentrazone. The best results were obtained using controlled pH (pH 4.0) and 1.0 g L(-1) of nanomaterials, resulting in 100 % conversion in only 30 min. Kinetic studies were also conducted, evaluating the influence of different nanoparticle dosages (1.0 to 4.0 g L(-1)), system temperatures (20 to 35 °C) and nickel levels in the composition of the nanomaterials (0.025 to 0.10 gNi/gFe). The mechanism of sulfentrazone conversion has changed due a direct reduction on the catalytic activity sites and indirect reduction by atomic hydrogen. Both mechanisms have followed pseudo-first order models. The conversion rate improved when the dosage of the nanomaterials, system temperature and nickel content in the composition of the nanocomposites were increased. Finally, the conversion products were elucidated by mass spectrometry and toxicity assays were performed using Daphnia Similis. The results showed that the dechlorination product is less toxic than sulfentrazone.