The objective of this study was to synthesize and characterize epigallocatechin-3-gallate (EGCG)-loaded/poly(D-L lactide-co-glycolide) acid (PLGA) microparticles, evaluate their effects on degree of conversion and release assay of adhesives, and subsequently to examine the resin-dentin bond strength of two EGCG formulations (free EGCG or loaded into PLGA microparticles) applied as a pretreatment or incorporated into an adhesive system. The formulations were prepared according to a PLGA:EGCG ratio of 16:1 using the spray-drying technique. The size and polydispersity index were determined by light scattering in aqueous dispersion. The degree of conversion (%DC) and release assay were assessed by Fourier transform infrared spectroscopy and ultraviolet-visible spectrophotometer, respectively. Subsequently, 45 third molars were divided into five groups (n=9) according to the different EGCG application modes and prepared for bond strength testing in a universal testing machine. Results demonstrated no statistically significant difference among the DC means after the PLGA microparticles were loaded with EGCG. For the release assay, the 1.0% PLGA/EGCG group presented better results after being elected for use in the bond strength test. The resin-dentin bond strengths of the experimental groups after 12 months of water storage were significantly higher than in the control group. EGCG could improve the durability of the resin-dentin bond over time and promote a new era for adhesive dentistry with the concept of controlled release.