RESUMO
In this paper, a new porous carbon material adsorbent was prepared using carbon microspheres assembled in hollow carbon spheres (HCS) with a hydrothermal method. Transmission electron microscopy, scanning electron microscopy, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, X-ray diffraction, and Raman spectroscopy were used to characterize the adsorbents. It was found that the diameter of carbon microspheres derived from 0.1 mol/L glucose was about 130 nm, which could be inserted inside HCS (pore size was 370-450 nm). The increase in glucose concentration would promote the diameter of carbon microspheres (CSs), and coarse CSs could not be loaded in the mesopores or macropores of HCS. Thus, the C0.1@HCS adsorbent had the highest Brunauer-Emmett-Teller surface area (1945 m2/g) and total pore volume (1.627 cm3/g). At the same time, C0.1@HCS posed a suitable ratio of micropores and mesopores, which could provide adsorption sites and volatile organic compound diffusion channels. Moreover, oxygen-containing functional groups -OH and CâO in CSs were also introduced into HCS, and the adsorption capacity and regenerability performance of the adsorbents were improved. The dynamic adsorption capacity of C0.1@HCS for toluene reached 813 mg/g, and the Bangham model was more suitable for describing the toluene adsorption process. The adsorption capacity was stably kept above 770 mg/g after eight adsorption-desorption cycles.