Synthesis of SiO2@Ag Nanocomposite for Investigating Metal-Enhanced Fluorescence and Surface-Enhanced Raman Spectroscopy.

SiO2@Ag nanocomposite (NC) has been synthesized by the chemical reduction and StÓ§ber method for Metal-enhanced fluorescence (MEF) of Rhodmine 6G (R6G) and Surface-enhanced Raman spectroscopy (SERS) of Malachite green (MG). As-synthesized SiO2@Ag NC indicated SiO2 nanosphere (NS) and Ag nanoparticle (NP) morphologies. The SiO2@Ag NC was high quality with a well-defined crystallite phase with average sizes of 24 nm and 132 nm for Ag NP and SiO2 NC, respectively. By using SiO2@Ag NC, the photoluminescence (PL) intensity of the R6G (at 59.17 ppm) was increased approximately 133 times. The SERS of the MG (at 1.0 ppm) with SiO2@Ag NC as substrate clearly observed vibrational modes in MG dye at 798, 916, 1172, 1394, and 1616 cm-1. As a result, the SERS enhancement factor (EFSERS) at 1172 cm-1 obtained 6.3 × 106. This initial study points to the potential of SiO2@Ag NC as a promising material for MEF and SERS substrates to detect dyes at low concentrations.

Defect-Induced Gas-Sensing Properties of a Flexible SnS Sensor under UV Illumination at Room Temperature.

Tin sulfide (SnS) is known for its effective gas-detecting ability at low temperatures. However, the development of a portable and flexible SnS sensor is hindered by its high resistance, low response, and long recovery time. Like other chalcogenides, the electronic and gas-sensing properties of SnS strongly depend on its surface defects. Therefore, understanding the effects of its surface defects on its electronic and gas-sensing properties is a key factor in developing low-temperature SnS gas sensors. Herein, using thin SnS films annealed at different temperatures, we demonstrate that SnS exhibits n-type semiconducting behavior upon the appearance of S vacancies. Furthermore, the presence of S vacancies imparts the n-type SnS sensor with better sensing performance under UV illumination at room temperature (25 °C) than that of a p-type SnS sensor. These results are thoroughly investigated using various experimental analysis techniques and theoretical calculations using density functional theory. In addition, n-type SnS deposited on a polyimide substrate can be used to fabricate high-stability flexible sensors, which can be further developed for real applications.