Alkali cation-induced cathodic corrosion in Cu electrocatalysts.

The reconstruction of Cu catalysts during electrochemical reduction of CO2 is a widely known but poorly understood phenomenon. Herein, we examine the structural evolution of Cu nanocubes under CO2 reduction reaction and its relevant reaction conditions using identical location transmission electron microscopy, cyclic voltammetry, in situ X-ray absorption fine structure spectroscopy and ab initio molecular dynamics simulation. Our results suggest that Cu catalysts reconstruct via a hitherto unexplored yet critical pathway - alkali cation-induced cathodic corrosion, when the electrode potential is more negative than an onset value (e.g., -0.4 VRHE when using 0.1 M KHCO3). Having alkali cations in the electrolyte is critical for such a process. Consequently, Cu catalysts will inevitably undergo surface reconstructions during a typical process of CO2 reduction reaction, resulting in dynamic catalyst morphologies. While having these reconstructions does not necessarily preclude stable electrocatalytic reactions, they will indeed prohibit long-term selectivity and activity enhancement by controlling the morphology of Cu pre-catalysts. Alternatively, by operating Cu catalysts at less negative potentials in the CO electrochemical reduction, we show that Cu nanocubes can provide a much more stable selectivity advantage over spherical Cu nanoparticles.

Calcium-mediated nitrogen reduction for electrochemical ammonia synthesis.

Ammonia (NH3) is a key commodity chemical for the agricultural, textile and pharmaceutical industries, but its production via the Haber-Bosch process is carbon-intensive and centralized. Alternatively, an electrochemical method could enable decentralized, ambient NH3 production that can be paired with renewable energy. The first verified electrochemical method for NH3 synthesis was a process mediated by lithium (Li) in organic electrolytes. So far, however, elements other than Li remain unexplored in this process for potential benefits in efficiency, reaction rates, device design, abundance and stability. In our demonstration of a Li-free system, we found that calcium can mediate the reduction of nitrogen for NH3 synthesis. We verified the calcium-mediated process using a rigorous protocol and achieved an NH3 Faradaic efficiency of 40 ± 2% using calcium tetrakis(hexafluoroisopropyloxy)borate (Ca[B(hfip)4]2) as the electrolyte. Our results offer the possibility of using abundant materials for the electrochemical production of NH3, a critical chemical precursor and promising energy vector.

Protocol for assembling and operating bipolar membrane water electrolyzers.

Renewable energy-driven bipolar membrane water electrolyzers (BPMWEs) are a promising technology for sustainable production of hydrogen from seawater and other impure water sources. Here, we present a protocol for assembling BPMWEs and operating them in a range of water feedstocks, including ultra-pure deionized water and seawater. We describe steps for membrane electrode assembly preparation, electrolyzer assembly, and electrochemical evaluation. For complete details on the use and execution of this protocol, please refer to Marin et al. (2023).1.

Development of a versatile electrochemical cell for in situ grazing-incidence X-ray diffraction during non-aqueous electrochemical nitrogen reduction.

In situ techniques are essential to understanding the behavior of electrocatalysts under operating conditions. When employed, in situ synchrotron grazing-incidence X-ray diffraction (GI-XRD) can provide time-resolved structural information of materials formed at the electrode surface. In situ cells, however, often require epoxy resins to secure electrodes, do not enable electrolyte flow, or exhibit limited chemical compatibility, hindering the study of non-aqueous electrochemical systems. Here, a versatile electrochemical cell for air-free in situ synchrotron GI-XRD during non-aqueous Li-mediated electrochemical N2 reduction (Li-N2R) has been designed. This cell not only fulfills the stringent material requirements necessary to study this system but is also readily extendable to other electrochemical systems. Under conditions relevant to non-aqueous Li-N2R, the formation of Li metal, LiOH and Li2O as well as a peak consistent with the α-phase of Li3N was observed, thus demonstrating the functionality of this cell toward developing a mechanistic understanding of complicated electrochemical systems.

Engineering Surface Architectures for Improved Durability in III-V Photocathodes.

GaInP2 has shown promise as the wide bandgap top junction in tandem absorber photoelectrochemical (PEC) water splitting devices. Among previously reported dual-junction PEC devices with a GaInP2 top cell, those with the highest performance incorporate an AlInP2 window layer (WL) to reduce surface recombination and a thin GaInP2 capping layer (CL) to protect the WL from corrosion in electrolytes. However, the stability of these III-V systems is limited, and durability continues to be a major challenge broadly in the field of PEC water splitting. This work provides a systematic investigation into the durability of GaInP2 systems, examining the impacts of the window layer and capping layer among single junction pn-GaInP2 photocathodes coated with an MoS2 catalytic and protective layer. The photocathode with both a CL and WL demonstrates the highest PEC performance and longest lifetime, producing a significant current for >125 h. In situ optical imaging and post-test characterization illustrate the progression of macroscopic degradation and chemical state. The surface architecture combining an MoS2 catalyst, CL, and WL can be translated to dual-junction PEC devices with GaInP2 or other III-V top junctions to enable more efficient and stable PEC systems.

Readily Constructed Glass Piston Pump for Gas Recirculation.

The recirculation of gases in a sealed reactor system is a broadly useful method in catalytic and electrocatalytic studies. It is especially relevant when a reactant gas reacts slowly with respect to residence time in a catalytic reaction zone and when mass transport control through the reaction zone is necessary. This need is well illustrated in the field of electrocatalytic N2 reduction, where the need for recirculation of 15N2 has recently become more apparent. Herein, we describe the design, fabrication, use, and specifications of a lubricant-free, readily constructed recirculating pump fabricated entirely from glass and inert polymer (poly(ether ether ketone) (PEEK), poly(tetrafluoroethylene) (PTFE)) components. Using these glass and polymer components ensures chemical compatibility between the piston pump and a wide range of chemical environments, including strongly acidic and organic electrolytes often employed in studies of electrocatalytic N2 reduction. The lubricant-free nature of the pump and the presence of components made exclusively of glass and PEEK/PTFE mitigate contamination concerns associated with recirculating gases saturated with corrosive or reactive vapors for extended periods. The gas recirculating glass pump achieved a flow rate of >500 mL min-1 N2 against atmospheric pressure at 15 W peak power input and >100 mL min-1 N2 against a differential pressure of +6 in. H2O (∼15 mbar) at 10 W peak power input.

A Spin Coating Method To Deposit Iridium-Based Catalysts onto Silicon for Water Oxidation Photoanodes.

Silicon has shown promise for use as a small band gap (1.1 eV) absorber material in photoelectrochemical (PEC) water splitting. However, the limited stability of silicon in acidic electrolyte requires the use of protection strategies coupled with catalysts. Herein, spin coating is used as a versatile method to directly coat silicon photoanodes with an IrOx oxygen evolution reaction (OER) catalyst, reducing the processing complexity compared to conventional fabrication schemes. Biphasic strontium chloride/iridium oxide (SrCl2:IrOx) catalysts are also developed, and both catalysts form photoactive junctions with silicon and demonstrate high photoanode activity. The iridium oxide photoanode displays a photocurrent onset at 1.06 V vs reversible hydrogen electrode (RHE), while the SrCl2:IrOx photoanode onsets earlier at 0.96 V vs RHE. The differing potentials are consistent with the observed photovoltages of 0.43 and 0.53 V for the IrOx and SrCl2:IrOx, respectively. By measuring the oxidation of a reversible redox couple, Fe(CN)63-/4-, we compare the charge carrier extraction of the devices and show that the addition of SrCl2 to the IrOx catalyst improves the silicon-electrolyte interface compared to pure IrOx. However, the durability of the strontium-containing photoanode remains a challenge, with its photocurrent density decreasing by 90% over 4 h. The IrOx photoanode, on the other hand, maintained a stable photocurrent density over this timescale. Characterization of the as-prepared and post-tested material structure via Auger electron spectroscopy identifies catalyst film cracking and delamination as the primary failure modes. We propose that improvements to catalyst adhesion should further the viability of spin coating as a technique for photoanode preparation.

Author Correction: A rigorous electrochemical ammonia synthesis protocol with quantitative isotope measurements.

An Amendment to this paper has been published and can be accessed via a link at the top of the paper.

A rigorous electrochemical ammonia synthesis protocol with quantitative isotope measurements.

The electrochemical synthesis of ammonia from nitrogen under mild conditions using renewable electricity is an attractive alternative1-4 to the energy-intensive Haber-Bosch process, which dominates industrial ammonia production. However, there are considerable scientific and technical challenges5,6 facing the electrochemical alternative, and most experimental studies reported so far have achieved only low selectivities and conversions. The amount of ammonia produced is usually so small that it cannot be firmly attributed to electrochemical nitrogen fixation7-9 rather than contamination from ammonia that is either present in air, human breath or ion-conducting membranes9, or generated from labile nitrogen-containing compounds (for example, nitrates, amines, nitrites and nitrogen oxides) that are typically present in the nitrogen gas stream10, in the atmosphere or even in the catalyst itself. Although these sources of experimental artefacts are beginning to be recognized and managed11,12, concerted efforts to develop effective electrochemical nitrogen reduction processes would benefit from benchmarking protocols for the reaction and from a standardized set of control experiments designed to identify and then eliminate or quantify the sources of contamination. Here we propose a rigorous procedure using 15N2 that enables us to reliably detect and quantify the electrochemical reduction of nitrogen to ammonia. We demonstrate experimentally the importance of various sources of contamination, and show how to remove labile nitrogen-containing compounds from the nitrogen gas as well as how to perform quantitative isotope measurements with cycling of 15N2 gas to reduce both contamination and the cost of isotope measurements. Following this protocol, we find that no ammonia is produced when using the most promising pure-metal catalysts for this reaction in aqueous media, and we successfully confirm and quantify ammonia synthesis using lithium electrodeposition in tetrahydrofuran13. The use of this rigorous protocol should help to prevent false positives from appearing in the literature, thus enabling the field to focus on viable pathways towards the practical electrochemical reduction of nitrogen to ammonia.

Lightly Fluorinated Graphene as a Protective Layer for n-Type Si(111) Photoanodes in Aqueous Electrolytes.

The behavior of n-Si(111) photoanodes covered by monolayer sheets of fluorinated graphene (F-Gr) was investigated under a range of chemical and electrochemical conditions. The electrochemical behavior of n-Si/F-Gr and np(+)-Si/F-Gr photoanodes was compared to hydride-terminated n-Si (n-Si-H) and np(+)-Si-H electrodes in contact with aqueous Fe(CN)6(3-/4-) and Br2/HBr electrolytes as well as in contact with a series of outer-sphere, one-electron redox couples in nonaqueous electrolytes. Illuminated n-Si/F-Gr and np(+)-Si/F-Gr electrodes in contact with an aqueous K3(Fe(CN)6/K4(Fe(CN)6 solutions exhibited stable short-circuit photocurrent densities of ∼10 mA cm(-2) for 100,000 s (>24 h), in comparison to bare Si electrodes, which yielded nearly a complete photocurrent decay over ∼100 s. X-ray photoelectron spectra collected before and after exposure to aqueous anodic conditions showed that oxide formation at the Si surface was significantly inhibited for Si electrodes coated with F-Gr relative to bare Si electrodes exposed to the same conditions. The variation of the open-circuit potential for n-Si/F-Gr in contact with a series of nonaqueous electrolytes of varying reduction potential indicated that the n-Si/F-Gr did not form a buried junction with respect to the solution contact. Further, illuminated n-Si/F-Gr electrodes in contact with Br2/HBr(aq) were significantly more electrochemically stable than n-Si-H electrodes, and n-Si/F-Gr electrodes coupled to a Pt catalyst exhibited ideal regenerative cell efficiencies of up to 5% for the oxidation of Br(-) to Br2.

Stable Solar-Driven Water Oxidation to O2(g) by Ni-Oxide-Coated Silicon Photoanodes.

Semiconductors with small band gaps (<2 eV) must be stabilized against corrosion or passivation in aqueous electrolytes before such materials can be used as photoelectrodes to directly produce fuels from sunlight. In addition, incorporation of electrocatalysts on the surface of photoelectrodes is required for efficient oxidation of H2O to O2(g) and reduction of H2O or H2O and CO2 to fuels. We report herein the stabilization of np(+)-Si(100) and n-Si(111) photoanodes for over 1200 h of continuous light-driven evolution of O2(g) in 1.0 M KOH(aq) by an earth-abundant, optically transparent, electrocatalytic, stable, conducting nickel oxide layer. Under simulated solar illumination and with optimized index-matching for proper antireflection, NiOx-coated np(+)-Si(100) photoanodes produced photocurrent-onset potentials of -180 ± 20 mV referenced to the equilibrium potential for evolution of O2(g), photocurrent densities of 29 ± 1.8 mA cm(-2) at the equilibrium potential for evolution of O2(g), and a solar-to-O2(g) conversion figure-of-merit of 2.1%.

Photoelectrochemical behavior of n-type Si(111) electrodes coated with a single layer of graphene.

The behavior of graphene-coated n-type Si(111) photoanodes was compared to the behavior of H-terminated n-type Si(111) photoanodes in contact with aqueous K3[Fe(CN)6]/K4[Fe(CN)6] as well as in contact with a series of outer-sphere, one-electron redox couples in nonaqueous electrolytes. The n-Si/Graphene electrodes exhibited stable short-circuit photocurrent densities of over 10 mA cm(-2) for >1000 s of continuous operation in aqueous electrolytes, whereas n-Si-H electrodes yielded a nearly complete decay of the current density within ~100 s. The values of the open-circuit photovoltages and the flat-band potentials of the Si were a function of both the Fermi level of the graphene and the electrochemical potential of the electrolyte solution, indicating that the n-Si/Graphene did not form a buried junction with respect to the solution contact.

Efficient synthesis of an eta2-pyridine complex and a preliminary investigation of the bound heterocycle's reactivity.

Pyridine borane is combined with TpW(NO)(PMe(3))(eta(2)-benzene) to form a complex of the heterocycle, which upon treatment with acetone and acid yields the pyridinium complex [TpW(NO)(PMe(3))(eta(2)-pyH(+))]OTf. Deprotonation in the presence of acetic anhydride delivers the N-acetylpyridinium complex as a 10:1 mixture of coordination diastereomers. This acylpyridinium resists reaction with water or oxygen but readily reacts with acetone, pyrrole, indole, or acrolein and a weak base to stereoselectively form 1,2-dihydropyridine complexes. Treatment of the indole-derived analogue with CuBr(2) results in liberation of 3-(pyridin-2-yl)-1H-indole.