High-speed infrared thermal measurements of impacted metallic solids.

The methodology used to measure transient temperature changes in impacted solids, using high-speed infrared detectors, is presented and discussed thoroughly. The various steps leading to a reliable measurement, namely selection of the sensing device, calibration of the setup, interfacing with the impact apparatus (Kolsky bar), and data reduction are presented. The outcome of the above methodology is illustrated in terms of the Taylor-Quinney factor, a well-known measure of the efficiency of the thermomechanical conversion.•Selection of infrared detectors.•Importance of the calibration procedure.•Determination of the Taylor-Quinney factor.

Reassessment of the Dynamic Thermomechanical Conversion in Metals.

Heat dissipation still remains an unsolved problem in dynamic plasticity, where nearly adiabatic conditions prevail during high-rate loading scenarios. It is well known that the mechanical energy that is not dissipated as heat during material straining remains stored in the lattice as microstructural defects, and thus, a one-to-one relationship can be expected between the stored energy, the materials microstructure, and its mechanical characteristics. This work demonstrates that this is not so straightforward. High-rate experiments on a Kolsky bar, combined with in situ thermal measurements, were performed on two well-studied materials: pure nickel and aluminum. A dislocation-based constitutive model was used to estimate the mechanical and thermomechanical material behavior. For both materials, the thermal response was observed to be strongly strain rate sensitive, while the mechanical flow, and microstructural characteristics (as characterized by transmission electron microscopy at similar strains), were not. This apparent discrepancy between mechanical and microstructural vs thermal results is discussed, and the concept of thermomechanical conversion is reassessed.