Magnetic Heating of Iron Oxide Nanoparticles and Magnetic Micelles for Cancer Therapy.

The inclusion of magnetic nanoparticles into block copolymer micelles was studied towards the development of a targeted, magnetically triggered drug delivery system for cancer therapy. Herein, we report the synthesis of magnetic nanoparticles and poly(ethylene glycol-b-caprolactone) block copolymers, and experimental verification of magnetic heating of the nanoparticles, self-assembly of the block copolymers to form magnetic micelles, and thermally-enhanced drug release. The semicrystalline core of the micelles melted at temperatures just above physiological conditions, indicating that they could be used to release a chemotherapy agent from a thermo-responsive polymer system. The magnetic nanoparticles were shown to heat effectively in high frequency magnetic fields ranging from 30-70 kA/m. Magnetic micelles also showed heating properties, that when combined with a chemotherapeutic agent and a targeting ligand could be developed for localized, triggered drug delivery. During the magnetic heating experiments, a time lag was observed in the temperature profile for magnetic micelles, likely due to the heat of fusion of melting of polycaprolactone micelle cores before bulk solution temperatures increased. Doxorubicin, incorporated into the micelles, released faster when the micelles were heated above the core melting point.

Polymer micelles with crystalline cores for thermally triggered release.

Interest in the use of poly(ethylene glycol)-b-polycaprolactone diblock copolymers in a targeted, magnetically triggered drug delivery system has led to this study of the phase behavior of the polycaprolactone core. Four different diblock copolymers were prepared by the ring-opening polymerization of caprolactone from the alcohol terminus of poly(ethylene glycol) monomethylether, M(n) ≈ 2000. The critical micelle concentration depended on the degree of polymerization for the polycaprolactone block and was in the range of 2.9 to 41 mg/L. Differential scanning calorimetry curves for polymer solutions with a concentration above the critical micelle concentration showed a melting endotherm in the range of 40 to 45 °C, indicating the polycaprolactone core was semicrystalline. Pyrene was entrapped in the micelle core without interfering with the ability of the polycaprolactone to crystallize. When the polymer solution was heated above the melting point of the micelle core, the pyrene was free to leave the core. Temperature-dependent measurements of the critical micelle concentration and temperature-dependent dynamic light scattering showed that the micelles remain intact at temperatures above the melting point of the polycaprolactone core.