RESUMO
Background: Zirconia has been used as a reliable core material in dental restorations for years; however, its bonding to resin cement is a matter of challenge. Physical, chemical, and combinations of these techniques have been investigated to boost the properties of zirconia surface bonding. The objective of this work was to evaluate the effect of hydroxyapatite coating as a chemical therapy in combination with physical modifications on the microshear bond strength of the resin cement over zirconia. Methods: In the present research, 60 sintered zirconia blocks (4 × 4 × 4 mm) were randomized into four groups of 15, including Al2O3 particle abrasion (group 1), HA coating (group 2), Al2O3 particle abrasion + HA coating (group 3), and Er, Cr: YSGG laser irradiation + HA coating (group 4). The microshear bond strength was determined by bonding the blocks to the resin cement. Results: The bond strengths (mean ± standard deviation) of modified zirconia surfaces were 16.93 ± 4.94 MPa, 16.14 ± 5.4 MPa, 19.4 ± 5.27 MPa, and 16.21 ± 3.7 MPa in groups 1-4, respectively. Test results of the ANOVA test revealed no significant difference regarding the bond strength values of zirconia surfaces to the resin cement between the studied preparation modalities (p > 0.05). Conclusion: Observations from the present study showed that HA coating can be as effective as the air-borne particle abrasion technique in improving bond strength to zirconia surfaces. Moreover, sandblasting by an aluminum oxide or Er, Cr: YSGG laser irradiation prior to HA coating of zirconia showed no significant effect on the reinforcement of bond strength values when compared to HA coating alone. The clinic hydroxyapatite coating alone or in combination with physical treatments improves the bond strength of zirconia to resin cement.
RESUMO
OBJECTIVES: Many advantages have been attributed to dental zirconia ceramics in terms of mechanical and physical properties; however, the bonding ability of this material to dental structure and/or veneering ceramics has always been a matter of concern. On the other hand, hydroxyapatite (HA) shows excellent biocompatibility and good bonding ability to tooth structure, with mechanically unstable and brittle characteristics, that make it clinically unacceptable for use in high stress bearing areas. The main purpose of this study was to introduce two simple yet practical methods to deposit the crystalline HA nanoparticles on zirconia ceramics. MATERIALS AND METHODS: zirconia blocks were treated with HA via two different deposition methods namely thermal coating and air abrasion. Specimens were analyzed by scanning electron microscopy, energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). RESULTS: In both groups, the deposition techniques used were successfully accomplished, while the substrate showed no structural change. However, thermal coating group showed a uniform deposition of crystalline HA but in air abrasion method, there were dispersed thin islands of HA. CONCLUSIONS: Thermal coating method has the potential to significantly alter the surface characteristics of zirconia. The simple yet practical nature of the proposed method may be able to shift the bonding paradigm of dental zirconia ceramics. This latter subject needs to be addressed in future investigations.
