Mobility and current boosting of In-Ga-Zn-O thin-film transistors with metal capping layer oxidation.

This study investigates the effect of an oxidized Ta capping layer on the boosting of field-effect mobility (µFE) of amorphous In-Ga-Zn-O (a-IGZO) Thin-film transistors (TFTs). The oxidation of Ta creates additional oxygen vacancies on the a-IGZO channel surface, leading to increased carrier density. We investigate the effect of increasing Ta coverage on threshold voltage (Vth), on-state current,µFEand gate bias stress stability of a-IGZO TFTs. A significant increase inµFEof over 8 fold, from 16 cm2Vs-1to 140 cm2Vs-1, was demonstrated with the Ta capping layer covering 90% of the channel surface. By partial leaving the a-IGZO uncovered at the contact region, a potential barrier region was created, maintaining the low off-state current and keeping the threshold voltage near 0 V, while the capped region operated as a carrier-boosted region, enhancing channel conduction. The results reported in this study present a novel methodology for realizing high-performance oxide semiconductor devices. The demonstrated approach holds promise for a wide range of next-generation device applications, offering new avenues for advancement in metal oxide semiconductor TFTs.

Improved high voltage operation of amorphous In-Ga-Zn-O thin film transistor by carrier density enhancement.

We report on improved high voltage operation of amorphous-In-Ga-Zn-O (a-IGZO) thin film transistors (TFTs) by increasing carrier density and distributing the high bias field over the length of the device which utilizes an off-set drain structure. By decreasing the O2partial pressure during sputter deposition of IGZO, the channel carrier density of the high voltage a-IGZO TFT (HiVIT) was increased to ∼1018cm-3. Which reduced channel resistance and therefore the voltage drop in the ungated offset region during the on-state. To further decrease the electric field in the offset region, we applied Ta capping and subsequent oxidation to locally increase the oxygen vacancy levels in the offset region thereby increasing local carrier density. The reduction of the drain field in the offset region from 1.90 Vµm-1to 1.46 Vµm-1at 200 V drain voltage, significantly improved the operational stability of the device by reducing high field degradation. At an extreme drain voltage of 500 V, the device showed an off-state current of ∼10-11A and on-state current of ∼1.59 mA demonstrating that with further enhancements the HiVIT may be applicable to thin-film form, low leakage, high voltage control applications.

Synthesis and PGE(2) production inhibition of 1H-furan-2,5-dione and 1H-pyrrole-2,5-dione derivatives.

3,4-Diphenyl-substituted 1H-furan-2,5-dione and 1H-pyrrole-2,5-dione derivatives were synthesized and evaluated for the inhibitory activities on LPS-induced PGE(2) production in RAW 264.7 macrophage cells. Both 1H-furan-2,5-dione and 1H-pyrrole-2,5-dione rings as main scaffolds were easily obtained using one of three synthetic methods. Among the compounds investigated, 1H-3-(4-sulfamoylphenyl)-4-phenyl-pyrrole-2,5-dione (6l) showed a strong inhibitory activity (IC(50)=0.61microM) of PGE(2) production.