Enhancing adhesion and alignment of human gingival fibroblasts on dental implants.

BACKGROUND: Promoting the directional attachment of gingiva to the dental implant leads to the formation of tight connective tissue which acts as a seal against the penetration of oral bacteria. Such a directional growth is mostly governed by the surface texture. MATERIAL AND METHODS: In this study, three different methods, mechanical structuring, chemical etching and laser treatment, have been explored for their applicability in promoting cellular attachment and alignment of human primary gingival fibroblasts (HGFIBs). RESULTS: The effectiveness of mechanical structuring was shown as a simple and a cost-effective method to create patterns to align HGIFIBs. CONCLUSION: Combining mechanical structuring with chemical etching enhanced both cellular attachment and the cellular alignment.

Fracture behaviour of implant-implant- and implant-tooth-supported all-ceramic fixed dental prostheses utilising zirconium dioxide implant abutments.

This in vitro study investigated the fracture behaviour of implant-implant-supported and implant-tooth-supported all-ceramic fixed dental prostheses (FDP) using zirconium dioxide implant abutments (FRIADENT® CERCON® abutments, DENTSPLY Friadent). Six different test groups (n = 8) were prepared. Groups 1, 2, 4, and 5 represented an implant-implant-supported FDP condition, whereas groups 3 and 6 simulated an implant-tooth-supported FDP condition. The second right premolar of the mandible was replaced with a pontic tooth. In groups 2 and 5, implant abutments were individualised by circumferential preparation. XiVe® S plus screw implants (DENTSPLY Friadent) that were 4.5 mm (first molar) and 3.8 mm (first premolar) in diameter and 11 mm in length and metal tooth analogues with simulated periodontal mobility, representing the first right premolar, were mounted in a polymethyl methacrylate block. The FDPs were cemented with KetacCem (3 M Espe GmbH, Germany). Groups 4, 5, and 6 were thermomechanically loaded (thermal and mechanical cycling (TCML) = 1.2 × 106; 10,000 × 5°/55°) and subjected to static loading until failure. Statistical analysis of data obtained for the force at fracture was performed using non-parametric tests. All samples tested survived TCML. In the implant-implant-supported groups, circumferential abutment preparation resulted in a tendency to lower fracture forces compared to groups with unprepared abutments (group 1, 472.75 ± 24.71 N; group 2, 423.75 ± 48.48 N; group 4, 647.13 ± 39.10 N; group 5, 555.86 ± 30.34 N). The implant-tooth-supported restorations exhibited higher fracture loads (group 3, 736.25 ± 82.23 N; group 6, 720.75 ± 48.99 N) than the implant-implant-supported restorations which did not possess circumferentially individualised abutments. Statistically significant differences were found when comparing the non-artificially aged groups. Implant-tooth-supported FDP restorations did exhibit an increased fracture load compared to implant-implant-supported FDP restorations.